Crown ethers are at their most basic level rings constructed of oxygen atoms linked by two- or three-carbon chains. They have attracted attention for their ability to selectively incorporate various atoms or molecules within the cavity formed by the ring. However, crown ethers are typically highly flexible, frustrating efforts to rigidify them for many uses that demand higher binding affinity and selectivity. Here we present atomic-resolution images of the same basic structures of the original crown ethers embedded in graphene. This arrangement constrains the crown ethers to be rigid and planar. First-principles calculations show that the close similarity of the structures should also extend to their selectivity towards specific metal cations. Crown ethers in graphene offer a simple environment that can be systematically tested and modelled. Thus, we expect that our finding will introduce a new wave of investigations and applications of chemically functionalized graphene.

Small angle neutron scattering (SANS) and scanning transmission electron microscopy (STEM) were used to study film formation by magnesium alloys AZ31B (Mg-3Al-1Zn base) and ZE10A (Elektron 717, E717: Mg-1Zn + Nd, Zr) in H₂O and D₂O with and without 1 or 5 wt% NaCl. No SANS scattering changes were observed after 24 h D₂O or H₂O exposures compared with as-received (unreacted) alloy, consistent with relatively dense MgO-base film formation. However, exposure to 5 wt% NaCl resulted in accelerated corrosion, with resultant SANS scattering changes detected. The SANS data indicated both particle and rough surface (internal and external) scattering, but with no preferential size features. The films formed in 5 wt% NaCl consisted of a thin, inner MgO-base layer, and a nano-porous and filamentous Mg(OH)₂ outer region tens of microns thick. Chlorine was detected extending to the inner MgO-base film region, with segregation of select alloying elements also observed in the inner MgO, but not the outer Mg(OH)₂. Modeling of the SANS data suggested that the outer Mg(OH)₂ films had very high surface areas, consistent with loss of film protectiveness. Implications for the NaCl corrosion mechanism, and the potential utility of SANS for Mg corrosion, are discussed.