Semi-crystalline shape memory polymers exhibit two-way shape memory effect (2W-SME) under constant stresses through crystallization-induced elongation upon cooling and melting-induced constriction upon heating. The applied constant stress influenced the prediction and usability of 2W-SME in practical applications without any external force. Here the reversible shape transition in EVA-shaped memory polymer was quantitative analyzed under a suitable temperature range and external stress-free condition. The fraction of reversible strain increased with increasing upper temperature ( T _high ) within the temperature range and reached the maximum value of 13.62% at 70 °C. However, reversible strain transition was almost lost when T _high exceeded 80 °C because of complete melting of crystalline scaffold, known as the latent recrystallization template. The non-isothermal annealing of EVA 2W-SMP under changing circulating temperatures was confirmed. Moreover, the orientation of crystallization was retained at high temperatures. These findings may contribute to design an appropriate shape memory protocol based on application-specific requirements.

Multiple-phase nanocomposites filled with carbon nanotubes (CNTs) have been developed for their significant potential in microwave attenuation. The introduction of other phases onto the CNTs to achieve CNT-based heterostructures has been proposed to obtain absorbing materials with enhanced microwave absorption properties and broadband frequency due to their different loss mechanisms. The existence of polyaniline (PANI) as a coating with controllable electrical conductivity can lead to well-matched impedance. In this work, a one-dimensional CNT@BaTiO3@PANI heterostructure composite was fabricated. The fabrication processes involved coating of an acid-modified CNT with BaTiO3 (CNT@BaTiO3) through a sol–gel technique followed by combustion and the formation of CNT@BaTiO3@PANI nanohybrids by in situ polymerization of an aniline monomer in the presence of CNT@BaTiO3, using ammonium persulfate as an oxidant and HCl as a dopant. The as-synthesized CNT@BaTiO3@PANI composites with heterostructures were confirmed by various morphological and structural characterization techniques, as well as conductivity and microwave absorption properties. The measured electromagnetic parameters showed that the CNT@BaTiO3@PANI composites exhibited excellent microwave absorption properties. The minimum reflection loss of the CNT@BaTiO3@PANI composites with 20 wt % loadings in paraffin wax reached −28.9 dB (approximately 99.87% absorption) at 10.7 GHz with a thickness of 3 mm, and a frequency bandwidth less than −20 dB was achieved from 10 to 15 GHz. This work demonstrated that the CNT@BaTiO3@PANI heterostructure composite can be potentially useful in electromagnetic stealth materials, sensors, and electronic devices.

Glass fiber fabrics/hollow glass microspheres (HGM)–waterborne polyurethane (WPU) textile composites were prepared using glass fiber, WPU, and HGM as skeleton material, binder, and insulation filler, respectively, to study the effect of HGM on the thermal insulation performance of glass fiber fabrics. Scanning electron microscopy, Instron 3367 tensile test instrument, thermal constant analysis, and infrared thermal imaging were used to determine the cross-sectional morphology, mechanical property, thermal conductivity, and thermal insulation property, respectively, of the developed materials. The results show that the addition of HGM mixed in WPU significantly enhanced thermal insulation performance of the textile composite with the reduction of thermal conductivity of 45.2% when the volume ratio of HGM to WPU is 0.8 compared with that of material without HGM. The composite can achieve the thermal insulation effect with a temperature difference of 17.74 °C at the temperature field of 70 °C. Meanwhile, the tensile strength of the composite is improved from 14.16 to 22.14 MPa. With these results, it is confirmed that designing hollow glass microspheres (HGM) is an effective way to develop and enhance the high performance of insulation materials with an obvious lightweight of the bulk density reaching about 50%.