A magnetic ZSM-5 zeolite with a core–shell type structure was synthesized, fully characterized and had its catalytic activity evaluated on the valorization of bio-derived furfuryl alcohol.

Food packaging based on nanotechnology of polymeric nanocomposites of graphene and graphene oxide results in packaging with better thermal, mechanical, antimicrobial, electrical packaging, moisture barrier and gas properties.

Understanding the basic properties of pristine carbon nitride electrodes is of great importance for their further applications as supercapacitor materials. To this end, a comparative study of unmodified carbon nitride is crucial to understand the difference between the bare material and its composite counterparts described in the literature. Therefore, the aim of this paper is to explore the electrochemical behaviour of casting-produced C₃N₄ electrodes using cyclic voltammetry, charge/discharge curves and impedance spectroscopy. The results from this study show a capacitance value of 113.7 F g⁻¹ at 0.2 A g⁻¹ with an impressive retention of 89.2% after 5000 charge and discharge cycles at 3.0 A g⁻¹. In addition, this material shows a large amount of specific energy (76.5 W h kg⁻¹) at an operation power of 11.9 W kg⁻¹, decreasing only 10.7% due to the electrochemical aging process. Hence, C₃N₄ constitutes a long-life pristine material with a large amount of energy and a moderate operation power with better performance than other C₃N₄-based composites found in the literature. These results are important to gain a better understanding of the inherent properties of carbon nitride – to further design composites with higher specific capacitance, longer lifetime, and specific energy.