Carbon nanomaterials, predominantly carbon nanofibers, carbon nanotubes, graphene, graphene nanoplates, graphene oxide and reduced graphene oxide, possess superior chemical, physical and mechanical properties. They have been successfully introduced into ordinary Portland cement to give enhancements in terms of mechanical properties, durability and electrical/thermal conductivity, and to modify the functional properties, converting conventional cement-based materials into stronger, smarter and more durable composites. This paper provides a comprehensive review of the properties of carbon nanomaterials, current developments and novel techniques in carbon nanomaterials enhanced cement-based composites (CN-CBCs). Further study of the applications of CN-CBCs at industrial scale is also discussed.

Multi-walled carbon nanotubes (MWCNTs) are promising nanoreinforcing materials for cement-based composites due to their superior material properties. Dispersion of MWCNTs is key for achieving the most effective way of enhancing efficiency, which is challenging in an alkaline cementitious environment. In this study, humic acid (HA) was used to stabilize the degree of dispersion of MWCNTs in an alkaline environment. The efficiency of HA in stabilizing MWCNT dispersion in cement composites was characterized using an ultraviolet spectrophotometer. The influences of HA on the workability and mechanical properties of ordinary Portland cement (OPC) reinforced with MWCNTs were evaluated, and the results revealed that the addition of HA can improve the stability of MWCNT dispersion in an alkaline environment. A concentration of 0.12 wt.% HA/S added to MWCNT suspensions was found to perform the best for improving the dispersion of MWCNTs. The addition of HA results in a decreased workability of the OPC pastes but has little influence on the strength performance. HA can affect the mechanical properties of OPC reinforced with MWCNTs by influencing the dispersion degree of the MWCNTs. An optimum range of HA (0.05–0.10 wt.%) is required to achieve the optimum reinforcing efficiency of MWCNTs.