Stabilization/solidification (S/S) is a low-cost and high-efficiency remediation method for contaminated soils, however, conventional cement-based S/S method has environmental constraints and sustainability concerns. This study proposes a low-carbon, cement-free, clay-based approach for simultaneous S/S of As and Pb in the contaminated soil, and accordingly elucidates the chemical interactions between alkali-activated clay binders and potentially toxic elements. Quantitative X-ray diffraction and 27Al nuclear magnetic resonance analyses indicated that the addition of lime effectively activated the hydration of kaolinite clay, and the presence of limestone further enhanced the polymerization of hydrates. X-ray photoelectron spectroscopy showed that approximately 19% of As[III] was oxidized to As[V] in the alkali-activated clay system, which reduced toxicity and facilitated immobilization of As. During the cement-free S/S process, As and Pb consumed Ca(OH)2 and precipitated as Ca3(AsO4)2·4H2O and Pb3(NO3)(OH)5, respectively, accounting for the low leachability of As (7.0%) and Pb (5.4%). However, the reduced amount of Ca(OH)2 decreased the degree of hydration of clay minerals, and the pH buffering capacity of the contaminated soil hindered the pH increase. Sufficient dosage of lime was required for ensuring satisfactory solidification and contaminant immobilization of the clay-based S/S products. The leachability of As and Pb in high-Ca S/S treated soil samples was reduced by 96.2% and 98.8%, respectively. This is the first study developing a green and cement-free S/S of As- and Pb-contaminated soil using clay minerals as an environmentally compatible binding material.

In this study, a magnesium oxide (MgO) coated corncob biochar (MCB) was synthesized by pyrolyzing MgCl2 pretreated corncob, for a better performance in lead immobilization in a contaminated soil compared with corncob biochar (CB). The properties and microstructures of CB and MCB were investigated. It was observed that MgO particles ranging from 1 to 2 μm were well coated on MCB, and the MgO content in MCB was calculated at 29.90% in w/w. The surface area of the biochar was significantly enhanced from 0.07 to 26.56 m2/g after the MgO coating. The MgO coating also significantly facilitated the lead removal percentage from 23% to 74% in aqueous solution by biochar. CB failed to immobilize lead in a soil washing residue and could not reduce its environmental risks in a laboratory incubation study. In contrast, MCB was applied to the soil and resulted in a significant reduction in TCLP leached lead from 10.63 to 5.24 mg/L (reduced by 50.71%). The comparison between MCB and other amendments suggests that the biochar component of MCB adsorbed lead onto its surface through cation-π interaction and increased surface adsorption due to higher surface area, and then the MgO coated on MCB's surface further enhanced the adsorption through precipitation. The synergistic roles of biochar-mineral composites make them a promising candidate for soil remediation.