Aim: To evaluate bond strength between RMGI and composite using different adhesive systems and curing techniques. Materials and Methods: Sixty prepared samples of RMGI were randomly divided into six groups according to adhesive systems (total-etch, two-step self-etch and all-in-one) and curing techniques (co-curing and pre-curing). In co-curing technique, the adhesive systems were applied on uncured RMGI samples and co-cured together. In the pre-curing technique, before application of adhesive systems, the RMGI samples were cured. Composite layers were applied and shear bond strength was measured. Two samples of each group were evaluated by SEM. Failure mode was determined by streomicroscope. Results: Both curing methods and adhesive systems had significant effect on bond strength (P-value < 0.05). There was an interaction between two factors (P-value <0.05). Both self-etch adhesives had significantly higher shear bond strength than the total-etch adhesive (P-value <0.05). The co-curing technique improved the bond strength in self-etch adhesives, but decreased the bond strength in total-etch adhesive (P-value<0.05). Conclusion: The application of self-etch adhesive systems and co-curing technique can improve the bond strength between the RMGI and composite.

Objective: To investigate the antimicrobial activity of colloidal selenium nanoparticles in chitosan solution (Cts-Se-NPs) against Streptococcus mutans, Lactobacillus acidophilus, and Candida albicans. Material and Methods: Cts-Se-NPs solution was prepared using a simple chemical reduction method. The MIC and MBC against S. mutans, L. acidophilus, and C. albicans were determined using the broth dilution assay. Results: The Cts-Se-NPs had remarkable antimicrobial activity against S. mutans, L. acidophilus, and C. albicans. The MIC values of the Cts-Se-NPs were lowest for S. mutans (0.068 mg/ml) compared to L. acidophilus (0.137 mg/ml), and C. albicans (0.274 mg/ml). The MBC values of the Cts-Se-NPs against the microorganisms after one, two, six, and 24 hours indicated that the concentration of 0.274 mg/ml of Cts-Se-NPs completely killed S. mutans, L. acidophilus, and C. albicans after one, two, and six hours, respectively. At the concentration of 0.137 mg/ml, S. mutans and L. acidophilus were killed after six and 24 hours, respectively. Conclusion: These findings encourage the potential use of Cts-Se-NPs in dentistry, while further clinical research is required in this area.

Introduction: Dentin hypersensitivity (DH) is a prevalent unpleasant condition which might affect quality of life. Laser therapy is one of the non-invasive treatments for dentin hypersensitivity. The aim of this umbrella review was to assess the effect of lasers on the treatment of dentin hypersensitivity by analyzing the previously published systematic reviews and meta-analyses. Methods: Electronic databases (PubMed, Embase, Scopus, Cochrane, and ISI) were searched to identify relevant systematic reviews and meta-analyses based on the keyword search strategy. Two independent reviewers carried out the selection of studies, extraction of data, and assessment of methodological quality. The actual overlap of primary studies was measured through the visual tool known as the citation matrix and three indices of % overlaps, covered area (CA), and corrected covered area (CCA). The reviews were appraised for methodological quality through A Measurement Tool to Assess Systematic Reviews (AMSTAR)-2, and the risk of bias was evaluated using the Risk of Bias in Systematic Reviews (ROBIS) tool. Results: Following eliminating duplicates, a total of 2,768 articles were found, and of them, 9 systematic reviews met the inclusion criteria. Six of them included a meta-analysis as well. The actual overlap of primary studies was low. The AMSTAR 2 tool classified one systematic review as high quality, three as moderate quality, three as low quality, and the remaining two as critically low quality. The results of the included reviews generally showed that all types of lasers reduced dentin hypersensitivity compared to placebo/no treatment. Conclusion: Lasers are effective in treating dentin hypersensitivity.

Saliva contamination is a major clinical problem in restorative procedures. The purpose of this study was to evaluate the effect of the time of salivary contamination during light curing on the degree of conversion and the microhardness of a restorative composite resin. Eight groups of 10 samples for measuring the microhardness and eight groups of 5 samples for evaluating the degree of conversion were prepared. The samples of each group were contaminated with human saliva at a certain time. The first group (T0) was contaminated before light curing. The specimens in groups T2–T30 were contaminated at 2, 5, 10, 15, 20 and 30 s after the start of light curing, respectively. The samples of group T40 were contaminated after light curing. The degree of conversion and the microhardness of the specimens were measured by Fourier transform infrared (FTIR) spectroscopy and Vickers hardness testing techniques, respectively. The results of this study revealed that there were no significant differences between the groups in terms of the degree of conversion of the composite resin. Consistent with the findings for the degree of conversion, significant differences in the microhardness between the groups were not found. In conclusion, from a clinical point of view, the results of our study showed that the time of salivary contamination (before, during or after light curing of composite resin) has no significant effect on the polymerization (degree of conversion) and one of the important mechanical properties of dental composite resins (microhardness).

To evaluate the bleaching procedure and application of sodium ascorbate on dentin bond durability, the enamel surface of intact human third molars (n = 18) were removed, and the teeth were randomly divided into two groups for immediate and six-month bond strength evaluation. The specimens were further assigned into three subgroups according to treatment procedure, as follows: subgroup A, no bleaching (positive control) was performed prior to the etch-and-rinse bonding with single bond and subsequent build-up with Z250 composite; subgroup B, the samples were bleached with 20% carbamide peroxide 6 h/day for five consecutive days prior to bonding; and subgroup C, bleaching was performed as in subgroup B, after which 10% sodium ascorbate was applied on dentin surface for 10 min before the bonding procedures. A microtensile bond strength test was performed and the failure modes were evaluated under a stereomicroscope. The data were analyzed using two-way analysis of variance (ANOVA) and Tukey’s post-hoc tests with a level of significance of 0.05. Bleaching significantly decreased the immediate and six-month bond strength. The application of sodium ascorbate had no significant effect on the immediate and six-month bond strength of bleached specimens. We conclude that the bleaching procedure may decrease the durability of the resin–dentin bond of the tested etch-and-rinse adhesive.

Background: To evaluate the effect of Ethanol Wet Bonding Technique (EWBT) on postoperative hypersensitivity (POH) of composite restorations in premolar teeth. Materials and Methods: In this randomized trial, 24 patients with at least three proximal carious lesions with similar axial depth and position of gingival floor in their premolars were enrolled. Following cavity preparation, the teeth were randomly assigned to one of three groups: (1) Class II resin-based composite (RBC) restoration using an etch-and-rinse adhesive + wet bonding technique (Control); (2) RBC restoration using EWBT + hydrophobic adhesive; and (3) RBC restoration using EWBT + hydrophilic adhesive. Tooth hypersensitivity was evaluated before and 1, 3, 7, 14 and 30 days after treatment according to the Visual Analog Scale. Data were analyzed statistically with Kruskal–Wallis and Friedman tests (P = 0.05). Results: All teeth showed similar levels of hypersensitivity after treatment (both P > 0.05). Furthermore, there was no difference between POH levels of the test and control groups at any control period (P < 0.05). Friedman test indicated that the POH significantly reduced within time in all groups (P < 0.05). Conclusion: Application of ethanol-wet bonding technique, either with hydrophobic or hydrophilic adhesives did not affect the POH of Class II composite restorations in premolars.