The 9–12% Cr ferritic–martensitic heat-resistant steel is the main candidate structural material for the Lead-cooled Faster Reactor. The lower Gibbs free energy change of Si oxide can promote the formation of a stable oxide layer, which can improve the corrosion resistance of the material. Therefore, it is of great significance to study the effect of silicon (Si) on the corrosion resistance of T91 steel in lead–bismuth eutectic (LBE). The corrosion resistance of T91 steel with Si contents of 0.5 wt.%, 1.3 wt.%, and 2.0 wt.%, both in dynamic and static LBE at 550 °C, was investigated. The microstructure was analyzed by X-ray diffraction (XRD), scanning electron microscope (SEM) and transmission electron microscope (TEM), while the oxide films were characterized by electron probe microanalysis (EPMA). Results show that the addition of Si is conducive to improving the corrosion resistance of T91 steel in LBE. T91 steel with high Si content has a thinner and more stable oxide film. The change of Si content can change the contact angle between the steel and LBE, and the contact angle is the largest when the Si content is 1.3 wt.%. The Si-rich oxide layer is usually located in the inner oxide layer, which promotes the formation of a Cr oxide layer located in the internal oxidation zone (IOZ). Si will not enter the precipitated phase, but only change the ferrite content. The oxidation model of T91 steel containing Si in LBE was also proposed.

This study investigates the influence of rare earth elements Ce and Y on the evolution of inclusions in T91 steel by melting experimental steels with varying Ce-Y contents in a vacuum induction melting furnace. The results show that the inclusions in the steel without rare earth are mainly composed of Mg-Al-O oxides, (Nb, V, Ti)(C, N) carbonitrides, and composite inclusions formed by carbonitrides coated oxides, and all of them have obvious edges and corners. Upon the addition of different concentrations of Ce and Y, the oxygen content in the steel significantly decreased, and the inclusions were modified into spherical rare earth oxides, sulfides, and oxy-sulfides. Additionally, no large-sized primary carbonitrides were observed. The average size of the inclusions was reduced from 2.8 μm in the non-rare-earth-added steel to 1.7 μm and 1.9 μm with rare earth addition. Thermodynamic analysis indicates that the possible inclusions precipitated in the steel with varying Ce contents include Ce₂O₃, Ce₂O₂S, Y₂O₃, Y₂S₃, and CeS. With the increase in Ce content, the rare earth inclusions Y₂S₃, Y₂O_3, and CeS can be transformed into Ce₂O₂S and Ce₂O₃. There are two kinds of reactions in the process of high-temperature homogenization: one is the internal transformation reaction of inclusions, which makes Y easier to aggregate in the inner layer, and the other is the reaction of Y₂S₃→CeS and Y₂O₃ + Y₂S₃→Ce₂O₂S due to the diffusion of Ce in the matrix to the inclusions. Combined with the mismatch analysis, it can be seen that Al₂O₃ has the best effect on the heterogeneous nucleation of carbonitrides during the solidification of molten steel. Among the rare earth inclusions, only Ce₂O₃ may become the nucleation core of carbonitrides, and the rest are more difficult to form heterogeneous nucleation. Therefore, by Ce-Y composite addition, increasing the Y/Ce ratio can reduce the formation of Ce₂O₃, which can avoid the precipitation of primary carbonitride and ultimately improve the dispersion strengthening effect. This study is of great significance for understanding the mechanism of rare earth elements in steel and provides theoretical guidance for the composition design and industrial trial production of rare earth steel.

In this study, the tensile properties, low-cycle fatigue behavior, and microscopic fatigue-failure mechanisms of 316H stainless steel in the temperature range of 600–800 °C were systematically investigated by means of tensile tests, high-temperature low-cycle fatigue tests, and scanning electron microscopy (SEM) analysis of fatigue fracture surfaces. Based on experimental data fitting, a life prediction model for the material in the high-temperature regime was established. The results indicate that the mechanical behavior of 316H stainless steel under both static and cyclic loading is significantly influenced by temperature and strain amplitude. Compared with its room-temperature properties, at 800 °C, the elastic modulus of 316H stainless steel decreases by approximately 30%, the tensile strength drops by about 60%, while the elongation after fracture increases by roughly 100%. Within the temperature range of 600–800 °C, the fatigue performance deteriorates with the increasing temperature, and the cyclic hardening rate accelerates as the temperature rises. The fracture mode in the instantaneous fracture zone of the fatigue fracture surface transitions from predominantly transgranular fracture to a mixed mode of transgranular and intergranular fracture as the temperature increases to 800 °C. Under higher strain amplitudes (around 0.6%), 316H stainless steel exhibits Masing behavior and dynamic strain aging (DSA). Correspondingly, the crack-initiation mode on the fatigue fracture surface shifts from a single surface source to multiple surface sources. A three-parameter model was employed to fit the strain–amplitude versus fatigue–life relationships of 316H stainless steel in the 600–800 °C range, showing good agreement with the experimental data, with most data points falling within a factor-of-two error band.