Pure copper’s exceptional thermal and electrical properties, along with its processability, make it indispensable in aerospace, automotive, and electrical industries, particularly in heat exchangers and radiators. Lattice structures, with high specific surface areas, low weight, and high strength, are ideal for lightweight yet strong components. While traditional methods struggle with complex lattice geometries, selective electron beam melting (SEBM) enables the fabrication of intricate pure copper lattices with high energy efficiency in a vacuum environment. This study used SEBM to fabricate OCTET pure copper lattices with relative densities of 21.16%–73.77%. The macrostructure matched the design, achieving a maximum energy absorption capacity of 15.00 MJ/m³. At 40.04% relative density, compressive response shifted from shock to compression hardening, with densification strains ranging from 23.96% to 51.68%. Microdefects such as corrugation, size differences, and internal holes influenced mechanical properties and energy absorption. Post-polishing reduced surface roughness from 14.12 μm to 2.70 μm without affecting specific energy absorption. Increasing strut diameter reduced the microdefects’ impact on lattice strength, enhancing performance and reliability.

Nickel-based superalloys are key materials for aerospace and gas turbine applications. Traditional manufacturing approaches struggle to produce controllable porous structures with complex topologies. This review focuses on additively manufactured porous Ni-based superalloys, and summarizes progress in porous structure design, including disordered, lattice, TPMS, bio-inspired, and AI-assisted structures. Common additive manufacturing technologies are introduced, along with their effects on microstructure evolution and defect formation. The review discusses non-equilibrium microstructures, elemental segregation, and typical defects such as lack-of-fusion, keyhole porosity, and residual stress, as well as their influences on strength, fatigue, and creep behavior. Post-processing strategies for defect mitigation and performance optimization are also summarized. This review highlights the unique mechanical and physical behavior of porous structures compared to bulk materials, with an emphasis on anisotropy, stress localization, and defect sensitivity. Finally, several critical and specific challenges are identified, including multi-scale modeling, microstructure control in complex topologies, fatigue prediction, and physics-constrained AI design. This review aims to provide a clear, focused, and structurally consistent overview of the current state of the field, and to support future research on additively manufactured porous Ni-based superalloys.

Porous ceramics have shown great application potential in aerospace, electronics, and lithium-ion battery thermal management due to their low density, high specific strength, and excellent thermal insulation. Material Jetting (MJ), a high-precision 3D printing technology, enables the fabrication of porous ceramics with tailored pore structures, but the synergistic effects of pore structure parameters (configuration, porosity, and number of periods) on their thermal insulation performance remain insufficiently explored. This study systematically investigates the thermal insulation behavior of zirconia porous ceramics fabricated by MJ through experimental tests and numerical simulations. Three typical lattice configurations (Octet, Schwarz, and Gyroid) were selected, and samples with varying porosities (40%, 50%, 60%) and numbers of periods (1, 2, 3) were prepared. The results indicate that the Octet configuration (60% porosity, 3 periods) exhibits the optimal thermal insulation performance, with a minimum cold-end temperature of 58.5 °C (experiment) and 59.21 °C (simulation), attributed to its strut-based structure that forms a more tortuous heat conduction path. For the Gyroid configuration, thermal insulation performance improves with increasing porosity (reducing solid conduction dominance under non-forced convection) and decreases with decreasing number of periods (due to inhomogeneous pore distribution extending heat transfer paths). Notably, the trend of porosity affecting thermal insulation is opposite to that of compressive performance. Numerical simulation results are consistent with experimental data in both values and trends, verifying the reliability of the model. This work clarifies the key factors regulating the thermal insulation of MJ-fabricated porous ceramics and provides practical structural design guidelines for applications such as lithium-ion battery thermal runaway management.

Porous ceramics have garnered widespread attention in high-temperature insulation, aerospace, and other fields due to their excellent thermal stability, low density, and superior thermal insulation performance. However, traditional preparation technologies suffer from limitations such as poor pore structure controllability, unstable mechanical properties, and long production cycles. In recent years, 3D printing (additive manufacturing) technology has emerged as a disruptive approach to address these challenges, enabling precise fabrication of porous ceramics with complex structures and tailored properties. This review comprehensively summarizes the research progress on 3D-printed porous ceramics, focusing on preparation technologies, structure optimization, and performance regulation. First, the principles and drawbacks of traditional preparation methods are analyzed. Then, four mainstream 3D printing technologies (Binder Jetting, Material Extrusion, Vat Photopolymerization, and Material Jetting) for porous ceramics are elaborated on in terms of forming mechanisms, process characteristics, typical cases, and performance advantages/disadvantages. Additionally, the structure–property optimization strategies, including the design of Triply Periodic Minimal Surface structures and the application of computational modeling and simulation, are discussed to achieve the balance between thermal insulation and mechanical properties. Finally, current challenges and future development trends of 3D-printed porous ceramics are prospected. This review provides a systematic reference for the rational selection of preparation technologies, structural design, and performance optimization of porous ceramics, promoting their engineering applications in high-value fields.