Honeycomb sandwich panels are utilized in many industrial applications due to their high bending resistance relative to their weight. Defects between the core and the facesheet compromise their integrity and efficiency due to the inability to transfer loads. The material system studied in the present paper is a unidirectional carbon fiber composite facesheet with a honeycomb core with a variety of defects at the interface between the two material systems. Current nondestructive techniques focus on defect detectability, whereas the presented method uses high-frequency ultrasound testing (UT) to detect and quantify the defect geometry and defect type. Testing is performed using two approaches, a laboratory scale immersion tank and a novel portable UT system, both of which utilize only single-side access to the part. Coupons are presented with defects spanning from 5 to 40 mm in diameter, whereas defects in the range of 15–25 mm and smaller are considered below the detectability limits of existing inspection methods. Defect types studied include missing adhesive, unintentional foreign objects that occur during the manufacturing process, damaged core, and removed core sections. An algorithm is presented to quantify the defect perimeter. The provided results demonstrate successful defect detection, with an average defect diameter error of $0.6$ mm across all coupons studied in the immersion system and 1.1 mm for the portable system. The best accuracy comes from the missing adhesive coupons, with an average error of $0.3$ mm. Conversely, the worst results come from the missing or damaged honeycomb coupons, with an error average of 0.7 mm, well below the standard detectability levels of 15–25 mm.

This study investigates ultrasonic wave propagation in carbon fiber reinforced polymer (CFRP) composites containing foreign object debris (FOD) by introducing a novel method to characterize the depth and size of FOD, from a single captured waveform generated by an out-of-focus spherically focused transducer. Current methods of inspection utilize a raster approach to both detect and quantify FOD, which is limited to identifying FOD smaller than 4 mm. The method introduced in the present paper allows for a single point scan to detect and quantify FOD, as small as 0.5 mm, with the highest error in the depth estimation being less than 8%. This paper presents experimental testing to inform a finite element analysis of a full waveform simulation of an immersion tank inspection environment and compares waveforms between testing and simulation. A transient pressure acoustic model is developed in the COMSOL Multiphysics environment to simulate wave propagations. Simulation results provide waveform reflection and transmission at material interfaces, which will occur when there is an acoustic mismatch between materials. The transmitted ultrasonic wave is partially reflected toward the transducer upon encountering material interfaces between the water, CFRP laminate, and the FOD. Simulation results show that the acoustic profile and pressure of the reflected wave captured by the transducer allows an accurate identification of FOD depth and size within the composite structure, suggesting an alternative method of inspection to quantify FOD characteristics faster than through conventional approaches. Results show an increase in captured signal pressure of over 125% between the 0.5 mm FOD and the 1 mm FOD located on the mid-plane of the laminate, and 500% between the same 0.5 mm FOD and 1 mm FOD placed near the front wall. These results suggest the potential sensitivity limits for physical component. This work demonstrates that small FOD, which are often difficult to resolve and quantify under conventional raster-based inspection, can be reliably identified by intentionally positioning the specimen within the defocused region of a spherically focused transducer. Results are presented to correlate the reflected acoustic pressure amplitude to defect depth, transducer–specimen distance, and FOD size, providing an approach to quantitatively discriminate small defects that would otherwise produce ambiguous signals.