The effects of the Cu content on the microstructure and strengthening mechanisms of the Al-Mg-Si-xCu alloys were systematically investigated using scanning electron microscopy (SEM), electron probe microanalysis (EPMA), transmission electron microscopy (TEM), and mechanical tensile tests. The results show that, the strengthening mechanisms change with the Cu content. For as-quenched alloys, solution strengthening (σ_SS) is predominant when the Cu content ≥2.5 wt.%, and of equivalent importance as grain size strengthening (σ_H-P) when the Cu content ≤1.0 wt.%. With respect to peak-aged alloys, precipitation strengthening (σ_ppt) is predominant when the Cu content ≥2.5 wt.%, but σ_SS becomes predominant when the Cu content is 4.5 wt.%. As the Cu content increases from 0.5 to 4.5 wt.%, the main type of precipitates in alloy tends to change from a β″ phase to Q′ phase, and then to a θ′ phase. Among the three types of precipitates, θ′-precipitate causes the largest increase in yield strength (σ_0.2) and the largest decrease rate in elongation. β″-precipitate leads to the smallest increase in σ_0.2 and the smallest decrease rate in elongation. The increase of Cu content reduces Si solubility in the Al matrix and thus decreases the nucleation rate of β″ phase during subsequent aging.

The effects of Gd, Y content on the microstructure and mechanical properties of Mg-Gd-Y-Nd-Zr alloy were investigated using hardness measurements, X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive spectrometer (EDS), and uniaxial tensile testing. The results indicate that the alloys in as-cast condition mainly consist of α-Mg matrix and non-equilibrium eutectic Mg_5.05RE (RE = Gd, Y, Nd). After solution treatment, the non-equilibrium eutectics dissolved into the matrix but some block shaped RE-rich particles were left at the grain boundaries and within grains. These particles are especially Y-rich and deteriorate the mechanical properties of the alloys. Both the compositions of the eutectic and the block shaped particle were independent of the total Gd, Y content of the alloys, but the number of the particles increases as the total Gd, Y content increases. The ultimate tensile strength increases as the total Gd, Y content decreases. A Mg-5.56Gd-3.38Y-1.11Nd-0.48Zr alloy with the highest ultimate tensile strength of 280 MPa and an elongation of 1.3% was fabricated. The high strength is attributed to the age hardening behavior and the decrease in block shaped particles.

The influences of cold rolling and subsequent heat treatment on the microstructure evolution of 2524 alloy were investigated using an orientation distribution function (ODF) and electron back-scattered diffraction (EBSD). A preparation method of 2524-T3 aluminum alloy with a strong Brass texture was developed, and its effect on the fatigue properties of the alloy was investigated using scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The results show that with the increase in cold rolling deformation from 0% to 80%, the volume fractions of Brass, copper, and S textures in the 2524-T3 alloy also increase, especially in the case of Brass and S textures. However, the volume fractions of cube and Goss textures are reduced significantly, especially for cube textures, which are decreased by 57.4%. Reducing coarse second-phase particles (CSPs) is conducive to the formation of a strong deformation texture during cold rolling. A 10% deformation at each rolling pass, followed by a step annealing, helps the preservation of a Brass texture even after solution treatment at 500 °C for 0.5 h, while a large cold deformation followed by high-temperature annealing helps the formation of a strong cube texture. The Brass texture can enhance the strength while decreasing the fatigue crack growth resistance of this alloy.