In this study, a series of MgAl–layered double hydroxide (LDH) thin films were synthesized by a single step hydrothermal process at different synthetic conditions on AA6082, and the combined effect of reaction temperatures and crystallization times on in situ growth MgAl–LDH structural geometry, growth rate, and more importantly on the corresponding corrosive resistance properties are briefly discussed. The synthesis of LDH was performed at reaction temperatures of 40, 60, 80, and 100 °C, while the treatment time was varied at 12, 18, and 24 h. The as-prepared synthetic coatings were characterized by scanning electron microscopy (SEM), energy dispersion spectroscopy (EDS), X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FT-IR), while the corresponding corrosion protection efficiency of the developed coating was studied through potentiodynamic polarization studies and electrochemical impedance spectra. The findings demonstrated that extended crystallization time and reaction temperature impart a significant effect on the oriented growth of layered double hydroxide, the surface morphology, and on the film thickness, which had a remarkable influence on the LDH corrosion resistance ability. The LDH coated specimen developed at 100 °C for 18 h reaction time showed a more compact and dense structure compared to the traditional platelet structure obtained at 80 °C for 24 h crystallization time, and interestingly that compact structure exhibited the lowest corrosion current density, up to five orders of magnitude lower than that of bare AA6082.

This work reviews the characteristics of layered double hydroxides (LDHs) in the context of protective thin films to enhance the corrosion resistance properties of aluminum alloys. A discussion is made in detail about the LDH protection mechanism and the effect of synthesis approaches on LDH structural variations and the corresponding anti-corrosion behavior. LDHs anion-exchange behavior to host inorganic/organic anions makes them a potential material to investigate for anti-corrosion film. This unique advantage and the availability of a wide range of metal oxide-based layers, interlayer anions, and self-healing properties make LDH family an attractive choice for the development of compact LDHs based smart coating systems.

In this study, a calcium–aluminum-layered double hydroxide (CaAl-LDH) thin film was grown on an AA6082 aluminum alloy, for the very first time, by using a facile in situ growth method in an effort to investigate the CaAl-LDH structural geometry and corresponding corrosion resistance properties. The structure and surface morphologies of the CaAl-LDH thin film were studied using a scanning electron microscope (SEM) equipped with an EDS detector, a transmission electron microscope (TEM), an X-ray diffractometer (XRD), and a Fourier transform infrared spectrometer (FT-IR), while the electron impendence spectra (EIS) and potentiodynamic curves were recorded to understand the LDH anticorrosion behavior. The findings demonstrated that thin, well-developed CaAl-LDH coatings with different surface morphologies can be prepared with eminent corrosion resistance properties. Specifically, the CaAl-LDH thin film synthesized at 140 °C–24 h synthetic conditions showed a large impedance modulus of 7.3 Ω cm² at 0.01 Hz (|Z|_f = 0.01 Hz), along with a low corrosion current density (I_corr) of 0.0007 μA cm⁻², while a vertically orientated rod like structure with a uniform surface morphology was observed.

In this work, various NiAl-LDH thin films, exhibiting specific surface morphologies, were developed directly on aluminum AA 6082 substrate to understand the two main characteristics of layered double hydroxide (LDH), i.e., ion-exchange behavior and barrier properties, which are found to have a significant influence on the LDH corrosion resistance properties. The as-prepared NiAl-LDH films were analyzed through the scanning electronic microscope (SEM), X-ray diffraction (XRD), while the corrosion behavior of the synthesized films was investigated by the electrochemical impedance spectroscopy (EIS) and potentiodynamic curves. The results indicated that NiAl-LDH microcrystals grow in various fashions, from porous relatively flat domains to well-developed platelet structure, with the variation of nickel nitrate to ammonium nitrate salts molar ratios. The LDH structure is observed in all cases and is found to cover the aluminum surface uniformly in the lamellar order. All the developed NiAl-LDHs are found to enhance the corrosion resistance of the aluminum substrate, specifically, a well-developed platelet structure is found to be more effective in chloride adsorptive and entrapment capabilities, which caused higher corrosion resistance compared to other developed NiAl-LDHs. The comparison of the synthesized NiAl-LDH morphologies on their ion-exchange capabilities, barrier effect and their combined effect on corrosion resistance properties is reported.