Hydrogen embrittlement is a complex phenomenon, involving several length- and timescales, that affects a large class of metals. It can significantly reduce the ductility and load-bearing capacity and cause cracking and catastrophic brittle failures at stresses below the yield stress of susceptible materials. Despite a large research effort in attempting to understand the mechanisms of failure and in developing potential mitigating solutions, hydrogen embrittlement mechanisms are still not completely understood. There are controversial opinions in the literature regarding the underlying mechanisms and related experimental evidence supporting each of these theories. The aim of this paper is to provide a detailed review up to the current state of the art on the effect of hydrogen on the degradation of metals, with a particular focus on steels. Here, we describe the effect of hydrogen in steels from the atomistic to the continuum scale by reporting theoretical evidence supported by quantum calculation and modern experimental characterisation methods, macroscopic effects that influence the mechanical properties of steels and established damaging mechanisms for the embrittlement of steels. Furthermore, we give an insight into current approaches and new mitigation strategies used to design new steels resistant to hydrogen embrittlement.

Titanium is a transition metal. It is present in several minerals including rutile and ilmenite, which are well dispersed over the Earth’s crust. Even though titanium is as strong as some steels, its density is only half of that of steel. Titanium is broadly used in a number of fields, including aerospace, power generation, automotive, chemical and petrochemical, sporting goods, dental and medical industries. The large variety of applications is due to its desirable properties, mainly the relative high strength combined with low density and enhanced corrosion resistance. This chapter discusses the applications of titanium and its alloys in the medical field.

Hydrogen diffusion and trapping in ferrite is evaluated by quantum mechanically informed kinetic Monte Carlo simulations in defective microstructures. We find that the lattice diffusivity is attenuated by two to four orders of magnitude due to the presence of dislocations. We also find that pipe diffusivity is vanishingly small along screw dislocations and demonstrate that dislocations do not provide fast diffusion pathways for hydrogen as is sometimes supposed. We make contact between our simulations and the predictions of Oriani's theory of ‘effective diffusivity’, and find that local equilibrium is maintained between lattice and trap sites. We also find that the predicted effective diffusivity is in agreement with our simulated results in cases where the distribution of traps is spatially homogeneous; in the trapping of hydrogen by dislocations where this condition is not met, the Oriani effective diffusivity is in agreement with the simulations to within a factor of two. This paper is part of a thematic issue on Hydrogen in Metallic Alloys