This study investigates the structural characteristics of SFRC with different amounts of steel fibers following exposure to freeze–thaw cycles, while taking into account various levels of confinement pressure and rates of deformation. The focus of the research is to examine the dynamic mechanical properties of SFRC exposed to freeze–thaw cycles. The inclusion of steel fibers improves the strength of concrete during freeze–thaw cycles, with 1% steel fiber content being the most effective. Strain rate and confining pressure significantly impact the strength and failure mode of SFRC. The strength of concrete increases linearly with the strain rate. With no confining pressure, the cracks in the concrete specimen align with the direction of the applied stress. And with confining pressure, concrete exhibits diagonal shear failure. Microstructural analysis results from scanning electron microscopy are consistent with the macroscopic properties.

To investigate the impact of freeze–thaw damage on the mechanical properties of concrete, this study utilized Python in combination with ABAQUS 2016 to generate a two-dimensional meso-scale model of concrete. Uniaxial compression tests were conducted on the concrete after freeze–thaw cycles to study the evolution of its mechanical properties. Using “relative compressive strength” as a variable, the relationships between this variable and the parameters of the freeze–thaw damage model were determined, leading to the establishment of the freeze–thaw damage model and the simulation of compressive tests on concrete after freeze–thaw cycles. This study also explored the changes in the mechanical properties of concrete with variations in ITZ parameters and coarse aggregate content. The conclusions drawn are as follows: A comparison with experimental data showed that the model ensures that the relative error of each mechanical property parameter does not exceed 7%, verifying the model’s rationality. Increasing the ratio of ITZ parameters improved the mechanical properties of the ITZ, enhancing the overall mechanical performance, but had almost no effect on the elastic modulus. Compared to ratios of 0.7 and 0.8, concrete with a ratio of 0.9 showed slower rates of decrease in compressive strength and elastic modulus and slower rates of increase in peak compressive strain after freeze–thaw cycles. The increase in coarse aggregate content had a similar effect on the strength and freeze–thaw resistance of concrete as the ratio of ITZ parameters. Concrete with a coarse aggregate content of 60% exhibited slower rates of change in mechanical properties after freeze–thaw cycles.

To address the challenges encountered during the in situ welding reinforcement process of hollow spherical joints, including complex construction, limited quality control, and low efficiency, this study proposed a prefabricated reinforced hollow spherical joint. A three-dimensional finite element (FE) model was developed and validated against experimental results to quantify the effects of T-rib web width (b), web thickness (t₁), ferrule thickness (t₂), hollow-sphere diameter (D), and bolt pretension (f_v) on the bearing capacity of the prefabricated joint. Based on these analyses, a predictive model was established for the axial compressive bearing capacity of the prefabricated joint. The results showed that, under compression, the reinforcing components primarily provided a supporting role to the hollow sphere, thereby improving the buckling resistance of the prefabricated joint under compression. The reinforcement mechanism primarily relied on friction between the ferrule and the steel stub for load transfer, with the available frictional resistance governed primarily by bolt pretension and the stiffness of the reinforcing components. When sufficient friction existed between the ferrule and the steel tube, increasing the T-rib web width from 0 mm to 80 mm improved the bearing capacity of the prefabricated joint by 33%. At a T-rib flange height (h)-to-web width ratio of h/b = 1.0, the T-rib satisfied the reinforcement requirement through its inherent strength and stiffness. As the hollow-sphere diameter-to-thickness ratio decreased, the incremental gain in bearing capacity diminished. A predictive model was proposed for compressive bearing capacity by accounting for the support provided by the reinforcing components and the effects of hollow-sphere diameter, steel-tube diameter, and the tube-to-sphere diameter ratio. The proposed model predicted the FE results with errors within ±10%, and the findings can provide a practical reference for designing the compressive bearing capacity of prefabricated reinforced hollow spherical joints.

This paper proposes a new type of variable-cross-section replaceable link that can isolate the plastic deformation. The link and the frame beam connect with the expanding section by a bolt along the flange and web separately. It is easy to design an elastic bolt, reduce bolt slippage, and facilitate link replacement after an earthquake. Considering the large elastic deformation range of high-strength steel and the superior plastic deformation of the new type of replaceable link, a high-strength eccentrically braced steel frame with a variable-section replaceable link is raised by setting a new type of variable-section replaceable link in the eccentrically braced steel frame. Then, the existing end plate connection replaceable link test specimen is simulated and verified by using ABAQUS software. The finite element model of the high-strength eccentrically braced steel frame with a variable-cross-section replaceable link is established, and the bearing capacity, stiffness, plastic rotation, plastic distribution, and other bearing mechanisms of the structure are studied by cyclic loading. The length of the energy-consuming region (e), the steel strength of the link and other components, and the length of the replaceable link (e’) are compared and analyzed with regard to the seismic performance of the structure. The results are of great significance for understanding and exploring the force mechanism, energy dissipation characteristics of the new variable-section replaceable link, and the seismic performance of the high-strength eccentrically braced steel frame, and it also provides a reference for subsequent research.