TiAlSiN/AlSiN coatings, with 3 and 30 periods, were successfully deposited by cathodic-arc evaporation technology. The composition, structure, mechanical, and tribological properties were studied at thermal treatment from 700 °C to 900 °C. The SEM observation and EDS analysis verified the dense structure and stable element composition in the coating depth at increased temperatures. A limited surface oxidation was identified at 800 °C, which increased moderately at a higher temperature of 900 °C. The coating period displays a nanocomposite structure of TiAl(Si)N and AlN nanograins incorporated in an amorphous Si₃N₄ matrix obtained by XRD and XPS analyses. The coatings exhibit high hardness of 41.1 GPa and 36.4 GPa for the 3- and 30-period coatings, respectively. The coatings with higher modulation periods demonstrate an excellent high temperature hardness and resistance to elastic and plastic deformations up to 900 °C. The hardness of the coatings with a smaller modulation period reduces to 29.7 GPa at the same temperature, causing a decrease in the H/E and H³/E^*2 ratios. The tribological tests found that the high-temperature wear resistance depends strongly on the coating composition and architecture. An oxidation wear mechanism dominates the coatings with a large modulation period, and the wear rate decreases with a temperature increase. Abrasive wear is predominant in coatings with a lower modulation period, leading to an increasing wear rate. Wear rate values of 7.27 × 10⁻⁶ mm³/N·m and 8.53 × 10⁻⁶ mm³/N·m were determined after annealing at 900 °C for the 3- and 30-period coatings, respectively.

This work focuses on the study of tribo-mechanical and microstructural properties of TiCN/ZrCN multilayer coatings with a modulation period of 12 nm, obtained by a conventional cathodic arc technique. The coatings were deposited at a temperature of 320 °C using nitrogen and methane reactive gases (N₂/CH₄) mixture in three different proportions. Surface morphology, composition, hardness, adhesion, friction and wear behavior were studied using atomic force microscopy, scanning electron microscopy with energy dispersive spectroscopy, X-ray diffraction, Raman spectroscopy, nanoindentation, and scratch and wear tests. The analysis of the coating composition revealed a strict dependence of the carbon content on the CH₄ flow rate. It was found that the coatings with a carbon content of 14.6 at.% and 15.9 at.% consist of crystalline TiZr (C,N) with the presence of amorphous carbon. All the studied TiCN/ZrCN coatings showed improved tribo-mechanical properties compared to TiN/ZrN multilayers obtained under the same deposition conditions. The highest hardness of 40 GPa was obtained for the coating deposited at a N₂/CH₄ flow rate of 370/100 sccm. The lowest wear rate of 3.16 × 10⁻⁶ mm³/N·m under dry sliding conditions was observed in the multilayer coatings deposited at the N₂/CH₄ flow rates of 330/140 sccm.

In this work, a non-standardized hypereutectic aluminum–silicon alloy AlSi21Cu5MgCr intended for the automotive industry is presented. The modification of the alloy is performed with the conventional modifier phosphorus in an amount of 0.04 wt%. The applied metallurgical treatment is the basis for the obtained modified structure. It has been established that after conducting the T6 heat treatment, the free silicon crystals are reduced to 26.9 µm, and the eutectic silicon crystals are spherical in shape and have dimensions not exceeding 8 µm. The macrohardness of the studied alloy is 168.5HV_10/10, a value significantly higher than that required for this type of alloy, which is in the range of 95 ÷ 137 HV (90 ÷ 130 HB). The microhardness of the α-phase in the composition of the eutectic is 154 µHV_50/10, which indicates that after quenching a saturated solid solution was fixed, and during the artificial aging process secondary strengthening phases were formed and separated. A CrAlN hard coating was deposited on the alloy surface. The mechanical properties of the coating were characterized by a hardness of 14 GPa, whereas the AlSi21Cu5MgCr substrate had a hardness of 2 GPa. The results showed considerable improvement of the hardness of the new alloy and well-tuned elastic–plastic properties. The obtained adhesive properties are compatible with this class of materials. The composition of the CrAlN hard coating is homogeneously distributed on the alloy surface and the morphology is improved. The investigations showed that CrAlN hard coatings could successfully be applied for the modification of the surface of AlSIMgCu alloys.