Blast furnace slag (SL) is an amorphous calcium aluminosilicate material that exhibits both pozzolanic and latent hydraulic activities. It has been successfully used to reduce the heat of hydration in mass concrete. However, SL currently available in the market generally experiences pre-treatment to increase its reactivity to be closer to that of portland cement. Therefore, using such pre-treated SL may not be applicable for reducing the heat of hydration in mass concrete. In this work, the adiabatic and semi-adiabatic temperature rise of concretes with 20% and 40% SL (mass replacement of cement) containing calcium sulfate were investigated. Isothermal calorimetry and thermal analysis (TGA) were used to study the hydration kinetics of cement paste at 23 and 50 °C. Results were compared with those with control cement and 20% replacements of silica fume, fly ash, and metakaolin. Results obtained from adiabatic calorimetry and isothermal calorimetry testing showed that the concrete with SL had somewhat higher maximum temperature rise and heat release compared to other materials, regardless of SL replacement levels. However, there was a delay in time to reach maximum temperature with increasing SL replacement level. At 50 °C, a significant acceleration was observed for SL, which is more likely related to the pozzolanic reaction than the hydraulic reaction. Semi-adiabatic calorimetry did not show a greater temperature rise for the SL compared to other materials; the differences in results between semi-adiabatic and adiabatic calorimetry are important and should be noted. Based on these results, it is concluded that the use of blast furnace slag should be carefully considered if used for mass concrete applications.

The search for new sources of high-quality non-crystalline silica as a construction material for high-performance concrete has attracted the interest of researchers for several decades. Numerous investigations have shown that highly reactive silica can be produced from rice husk, an agricultural waste that is abundantly available in the world. Among others, the production of rice husk ash (RHA) by chemical washing with hydrochloric acid prior to the controlled combustion process has been reported to provide higher reactivity because such a process removes alkali metal impurities from RHA and provides an amorphous structure with higher surface area. This paper presents an experimental work in which a highly reactive rice husk ash (TRHA) is prepared and evaluated as a replacement for Portland cement in high-performance concretes. The performance of RHA and TRHA was compared with that of conventional silica fume (SF). Experimental results showed that the increase in compressive strength of concrete with TRHA was clearly observed at all ages, generally higher than 20% of the strength obtained with the control concrete. The increase in flexural strength was even more significant, showing that concrete with RHA, TRHA and SF increased by 20%, 46%, and 36%, respectively. Some synergistic effect was observed when polyethylene–polypropylene fiber was used for concrete with TRHA and SF. The chloride ion penetration results also indicated that the use of TRHA had similar performance compared to that of SF. Based on the results of statistical analysis, the performance of TRHA is found to be identical to that of SF. The use of TRHA should be further promoted considering the economic and environmental impact that will be achieved by utilizing agricultural waste.