In this study, the effects of cryo-rolling on the corrosion resistance of commercial pure titanium were examined. Cryo-rolling was performed with thickness reductions of 20, 50, 70, and 85%. The samples were analyzed using X-ray diffraction, optical microscopy, and scanning electron microscopy. Corrosion behavior of the cryo-rolled samples in a 3.5 wt.% NaCl solution was assessed using potentio-dynamic polarization and electrochemical impedance spectroscopy. The results demonstrated that the grains become more refined as the amount of deformation increases. Based on potentio-dynamic polarization and electrochemical impedance spectroscopy results, the corrosion resistance of the cryo-rolled samples was significantly improved.