Superhydrophobic metal wires have shown great application prospects in oil–water separation, anti-corrosion, anti-icing, and other fields due to their excellent water repellency. However, how to fabricate a superhydrophobic surface on ultra-fine metal wire remains a challenge. Here, we proposed a method using laser processing to efficiently fabricate superhydrophobic ultra-fine brass wire. Firstly, we analyzed the mechanism of the laser processing of curved surfaces and designed a controllable angle rotation fixture to avoid the machining error caused by secondary positioning in the machining process. Then, we investigated the influences of the laser power, scanning speed, and scanning times on the surface morphology and wettability of the ultra-fine brass wire. The optimal laser processing parameters were obtained: laser power of 6 W, scanning speed of 500 mm/s, and scanning time of 1. After low surface energy modification, the water contact angle and surface roughness Sa of the ultra-fine brass wire were 156° and 1.107 μm, respectively. This work is expected to enrich the theory and technology for fabricating superhydrophobic ultra-fine brass wire.

GH3536 superalloy is widely used in the high-temperature components of aerospace applications for its excellent high-temperature strength and corrosion resistance. However, under such a harsh environment, surface defects can make the superalloy prone to corrosion and fatigue fractures. Therefore, it is important to eliminate surface defects through polishing. However, the existing polishing methods usually suffer from some issues such as surface integrity damage, low efficiency, and poor environmental sustainability. More importantly, these methods fail to account for the requirement of surface roughness below 0.05 μm in some high-precision aerospace components. Herein, the plasma electrolytic polishing (PEP) of GH3536 superalloy is systematically investigated and optimized through single-factor experiments and response surface methodology (RSM). A minimum surface roughness Ra of 0.044 μm with a mirror-like surface was achieved at a voltage of 303.8 V, electrolyte temperature of 66.2 °C, polishing time of 5 min, and submersion depth of 7.5 cm. At the same optimized condition, the material removal rate was 59.12 mg·min⁻¹. After polishing, the surface composition of GH3536 superalloy varied negligibly, while its corrosion resistance improved markedly, with a 53.72% increase in polarization resistance and a 43.46% decrease in corrosion current density. Meanwhile, the microhardness slightly decreased due to the removal of the work-hardened layer and the compressive residual stress exhibited a more uniform distribution across the surface, contributing to improved near-surface mechanical stability. This study establishes an optimized PEP parameter for improving the surface quality of GH3536 superalloy, offering a practical method for the precision finishing of aerospace-grade superalloy components.