Background/Aim. Bulimia is in many cases followed by frequent vomiting, which in long term can result in irreversible loss of dental tissue, most commonly manifested as dental erosion. Frequent purging, xerostomia, lack of oral hygiene and acidic environment are also suitable for caries development. The aim of the research was to determine the presence, localization and degree of dental erosion using Basic Erosive Wear Examination (BEWE) index system, as well as to determine the Decayed, Missing and Filled Teeth (DMFT) index in purging bulimic patients. Methods. The study involved 30 purging bulimic patients and 30 healthy subjects. Used methods were survey (questionnaire) and clinical examination. The clinical examination included intraoral inspection and assessment of dental status using BEWE and DMFT index. Results. On the bases of conducted research, it has been found that dental erosion are significantly more often present in purging bulimics compared to the controls (chi(2) = 5.963, p < 0.05), that eroded lesions are more severe in the bulimic group (t = 3.925, p < 0.05) and predominantly located on oral surfaces of the teeth (chi(2) = 10.561, p < 0.05). DMFT index values showed no significant difference between bulimic patients and controls (t = 0.741, p = 0.461). Conclusion. Dental erosion are often encountered in patients suffering purging bulimia, especially on oral surfaces of anterior teeth that come into direct contact with gastric acid, so many bulimics exhibit high values of erosive tooth wear on mentioned surfaces. DMFT index score did not show significant differences compared to healthy participants, but due to complexity of carious process further investigation is necessary.

Introduction/Objective. The aim of this paper was to verify the biocompatibility of the newly synthesized nanostructured material based on calcium aluminate after implantation into the subcutaneous tissue of rats. Methods. The study included 18 rats aged 10?11 weeks, divided into two experimental groups (n = 9). In all animals, incision took place on the back and two pockets of 15 mm in depth were made, in which sterile polyethylene tubes with test materials [calcium aluminate cement (ALBO-CA), calcium silicate cement with the addition of hydroxyapatite (ALBO-CSHA), and mineral trioxide aggregate (MTA) for the control group) were implanted. Six rats of each group were sacrificed in three observational periods (seven, 15, 30 days). Pathohistological analysis included inflammation, bleeding, fibrous capsule, and tissue integrity around the implanted material. Results. After seven days of treatment, ALBO-CA and ALBO-CSHA showed better tissue response compared to MTA, with a statistically significant difference in inflammation intensity (p = 0.2781). The difference in vascular congestion and thickness of the fibrous capsule after implantation of ALBO-CA material compared to MTA was also statistically significant (p = 0.5567). At the end of the 30-day evaluation period, an identical inflammatory response of connective tissue at the site of implanting ALBO-CA, ALBO-CSHA, and MTA (score of 0.7) was recorded. The formation of thick or moderately thick fibrous capsule was found to be the thickest in ALBO-CA (grade 3.7). There were no statistically significant differences between the parameters analyzed after 30 days. Conclusion. Newly synthesized ALBO-CA showed a satisfactory tissue response and confirmed biocompatibility after implantation in subcutaneous tissue of rats.

Background/Aim. Excessive consumption of acidic dietary substances, such as carbonated beverages, increased the chances of dental erosion. The aim of this study was to determine influence of carbonated beverages on enamel and dentin, during different intervals. Methods. Sixty samples were obtained from fifteen impacted third molars. Tooth crown was divided into four parts. One part was a control sample, immersed in destilled water and other three parts were the experimental samples, stored in the following tested beverages: carbonated water, Coca-Cola and Schweppes Bitter Lemon. For each beverage, pH was measured before immersion of the samples. The first group of twenty samples were analysed and photographed, using a Scanning Electron Microscope (SEM), after 60 minutes, the second group after 24 hours and the third group after 7 days of exposure to drinks. The enamel was analysed on the outer surface of the cusps and longitudinal section. Dentin was analysed on longitudinal section. An individually adopted scale was used for determination of the degree of erosive changes of these dental tissues. The data were analysed using the analysis of varance (ANOVA). Results. The pH levels of the tested beverages was bellow the critical pH for enamel demineralisation. The SEM images showed different intensity of erosive changes caused by the tested beverages. The analysis by ANOVA revealed a significant difference between all groups of the treated samples, after 60 minutes of exposure to beverages. The highest values of erosive changes showed the samples that were immersed in Schweppes Bitter Lemon. The analysis of the samples after 24 hours and 7 days showed that the samples immersed in Coca-Cola and Schweppes Bitter Lemon can be classified as one group that was statistically significantly different compared with the control samples and samples immersed in carbonated water. Conclusion. Prolonged exposure of dental tissue to carbonated beverages cause erosive changes and a loss of surface profile.