Chitosan, which is derived from chitin, is the only known natural alkaline cationic polymer. Chitosan is a biological material that can significantly improve the living standard of the country. It has excellent properties such as good biodegradability, biocompatibility, and cell affinity, and has excellent biological activities such as antibacterial, antioxidant, and hemostasis. In recent years, the demand has increased significantly in many fields and has huge application potential. Due to the poor water solubility of chitosan, its wide application is limited. However, chemical modification of the chitosan matrix structure can improve its solubility and biological activity, thereby expanding its application range. The review covers the period from 1996 to 2022 and was elaborated by searching Google Scholar, PubMed, Elsevier, ACS publications, MDPI, Web of Science, Springer, and other databases. The various chemical modification methods of chitosan and its main activities and application research progress were reviewed. In general, the modification of chitosan and the application of its derivatives have had great progress, such as various reactions, optimization of conditions, new synthetic routes, and synthesis of various novel multifunctional chitosan derivatives. The chemical properties of modified chitosan are usually better than those of unmodified chitosan, so chitosan derivatives have been widely used and have more promising prospects. This paper aims to explore the latest progress in chitosan chemical modification technologies and analyze the application of chitosan and its derivatives in various fields, including pharmaceuticals and textiles, thus providing a basis for further development and utilization of chitosan.

Chitosan is the only cationic polysaccharide found in nature. It has broad application prospects in biomaterials, but its application is limited due to its poor solubility in water. A novel chitosan derivative was synthesized by amidation of chitosan with 18β-glycyrrhetinic acid and sialic acid. The chitosan derivatives were characterized by Fourier transform infrared spectroscopy, thermogravimetric analysis, and measurement of the zeta potential. We also investigated the solubility, cytotoxicity, and blood compatibility of chitosan derivatives. 18β-glycyrrhetinic acid and sialic acid could be grafted onto chitosan molecular chains. The thermal stability of the synthesized chitosan derivatives was decreased and the surface was positively charged in water and phosphate-buffered saline. After chitosan had been modified by 18 β-glycyrrhetinic acid and sialic acid, the solubility of chitosan was improved greatly in water and phosphate-buffered saline, and percent hemolysis was <5%. Novel amphiphilic chitosan derivatives could be suitable polymers for biomedical purposes.

Creation of bio-multifunctional wound dressings with potent hemostatic, antibacterial, anti-inflammatory, and angiogenesis features for bolstering the healing of full-thickness wounds is sought after for clinical applications. We created bio-multifunctional composite sponges by coupling alginate and chitosan with Sargassum pallidum polysaccharides through electrostatic interactions, calcium ion (Ca²⁺) crosslinking, and lyophilization. Alginate/chitosan (AC) sponges with different concentrations of Sargassum pallidum polysaccharides were obtained and termed AC, ACS—1%, ACS—2.5%, and ACS—5%. ACS—1% and ACS—2.5% sponges exhibited uniform porosity, high water vapor transmission rate, high water absorption, as well as good hemostatic and antibacterial abilities. ACS—2.5% sponges facilitated wound closure and promoted angiogenesis and re-epithelialization in the dermis. These data suggest that ACS sponges containing a certain amount of Sargassum pallidum polysaccharides could be employed for treatment of full-thickness skin wounds.

Increasing the yield and purity of B-phycoerythrin (B-PE) can improve the economic state of microalgae industrial processing. One method of cost reduction involves the recovery of remaining B-PE from wastewater. In this study, we developed a chitosan (CS)-based flocculation technique for the efficient recovery of B-PE from a low concentration of phycobilin in wastewater. We investigated the effects of the molecular weight of chitosan, B-PE/CS mass ratio, and solution pH on the flocculation efficiency of CS and the effects of phosphate buffer concentration and pH on the recovery rate of B-PE. The maximum flocculation efficiency of CS, recovery rate, and purity index of B-PE were 97.19% ± 0.59%, 72.07% ± 1.37%, and 3.20 ± 0.025 (drug grade), respectively. The structural stability and activity of B-PE were maintained during the recovery process. Economic evaluation revealed that our CS-based flocculation method is more economical than the ammonium sulfate precipitation method is. Furthermore, the bridging effect and electrostatic interaction play important roles in B-PE/CS complex flocculation process. Hence, our study provides an efficient and economical method to recover high-purity B-PE from a low concentration of phycobilin in wastewater, which promoted the application of B-PE as a natural pigment protein in food and chemical applications.

Improving the transdermal absorption of weakly soluble drugs for topical use can help to prevent and treat skin photoaging. Nanocrystals of 18β-glycyrrhetinic acid (i.e., NGAs) prepared by high-pressure homogenization and amphiphilic chitosan (ACS) were used to form ANGA composites by electrostatic adsorption, and the optimal ratio of NGA to ACS was 10:1. Dynamic light scattering analysis and zeta potential analysis were used to evaluate the nanocomposites’ suspension, and the results showed that mean particle size was 318.8 ± 5.4 nm and the zeta potential was 30.88 ± 1.4 mV after autoclaving (121 °C, 30 min). The results of CCK-8 showed that the half-maximal inhibitory concentration (IC50) of ANGAs (71.9 μg/mL) was higher than that of NGAs (51.6 μg/mL), indicating that the cytotoxicity of ANGAs was weaker than that of NGAs at 24 h. After the composite had been prepared as a hydrogel, the vertical diffusion (Franz) cells were used to investigate skin permeability in vitro, and it was shown that the cumulative permeability of the ANGA hydrogel increased from 56.5 ± 1.4% to 75.3 ± 1.8%. The efficacy of the ANGA hydrogel against skin photoaging was studied by constructing a photoaging animal model under ultraviolet (UV) irradiation and staining. The ANGA hydrogel improved the photoaging characteristics of UV-induced mouse skin significantly, improved structural changes (e.g., breakage and clumping of collagen and elastic fibers in the dermis) significantly, and improved skin elasticity, while it inhibited the abnormal expression of matrix metalloproteinase (MMP)-1 and MMP-3 significantly, thereby reducing the damage caused by UV irradiation to the collagen-fiber structure. These results indicated that the NGAs could enhance the local penetration of GA into the skin and significantly improve the photoaging of mouse skin. The ANGA hydrogel could be used to counteract skin photoaging.