The joining of Ti-47Al-2Cr-2Nb using Ti-15Cu-15Ni (wt%) as braze alloy was investigated. Experiments were conducted at 980 and 1000°C for 10 min. The microstructure and the chemical composition of the interfaces were studied by scanning electron microscopy (SEM) and by energy dispersive X-ray spectroscopy (EDS), respectively. For both processing conditions the reaction between the γ-TiAl alloy and the braze alloy produced layered interfaces, which are essentially composed of α2-Ti3Al and of Ti-Ni-Cu-Al and Ti-Ni-Cu intermetallic compounds. Microhardness tests showed that all reaction layers are harder than either the γ or the (α2 + γ) lamellar grains of the intermetallic alloy.

Intermetallics and superalloys brazing development is a current topic owing the extending use of these alloys in industrial applications. In this work a γ-TiAl alloy was joined to Inconel 718 by active metal brazing, using Incusil-ABA as filler. Joining was performed at 730 °C, 830 °C and 930 °C, with a 10 min dwelling time. The interfaces were characterized by Scanning Electron Microscopy (SEM), Energy Dispersive X-ray Spectroscopy (EDS) and Electron Backscatter Diffraction (EBSD). For all processing conditions, the reaction between the base materials and the braze alloy produced multilayered interfaces. For all processing temperatures tested (Ag), (Cu), AlNi₂Ti and AlCu₂Ti were identified at the interface. Raising the brazing temperature increased the thickness of the interface and coarsened its microstructure. The increase of the extension of the interface was essentially due to the growth of the reaction layers formed near each base material, which were found to be mainly composed of intermetallic compounds. The mechanical behavior of the joints, at room temperature, was assessed by microhardness and shear tests. For all processing conditions the hardness decreases from periphery towards the Ag-rich centre of the joints. Brazing at 730 °C for 10 min produced the joints with the highest average shear strength (228±83 MPa). SEM and EDS analysis of the fracture surfaces revealed that fracture of joints always occurred across the interface, preferentially through the hard layer, essentially composed of AlNi₂Ti, resulting from the reaction between Inconel 718 and the braze alloy.

Joining γ-TiAl alloy to Ni-based superalloy Hastelloy using Ag-Cu sputtered coated Ti foil as brazing filler was investigated in this study. Brazing experiments were performed at 900, 950, and 980 °C with a dwelling stage of 10 min in vacuum. The microstructure and the chemical composition of the resulting interfaces were analyzed by scanning electron microscopy (SEM) and by energy dispersive X-ray spectroscopy (EDS), respectively. Sound joints were produced after brazing at 980 °C, presenting a multilayered interface, consisting mainly of Ti-Al and Ti-Ni-Al intermetallics close to the γ-TiAl alloy, and of Ti-rich, Ti-Ni, and Cr-Ni-Mo rich phases near Hastelloy. The hardness of the interface, ranging from around 300 to 1100 HV0.01, is higher than both base materials, but no segregation of either Ag solid solution or coarse intermetallic particles was observed. Therefore, the developed brazing filler also avoids the need to perform post-brazing heat treatments that aim to eliminate detrimental extensive segregation of either soft phases or of hard and brittle compounds.