Al-Li based alloys are attractive materials for the aerospace industry. The twin-roll casting of such materials could provide properties not achievable by conventional direct-chill casting and downstream processing methods due to significantly higher solidification rates. An Al-Li-Cu-Mg-Zr alloy was twin-roll cast with the same alloy containing a small addition of Sc. The microstructure of as-cast materials and the influence of Sc on the behavior of the alloy at elevated temperatures were studied by means of light and electron microscopy and by resistivity measurements. A fine-grained structure was formed during twin-roll casting, but several surface and internal defects were found on the strips, which should be suppressed by a further adjustment of the casting conditions. The addition of Sc had a positive effect on grain size uniformity and microstructure stabilization at elevated temperatures, as shown by the precipitation of a fine dispersion of coherent Sc- and Zr-containing precipitates.

The sintering dynamics of nickel nanoparticles (Ni NPs) were investigated through a comprehensive approach that included in situ transmission electron microscopy annealing and molecular dynamics simulations. This study systematically examines the transformation behaviors of Ni NP agglomerates over a temperature spectrum from room temperature to 850 °C. Experimental observations, supported by molecular dynamics simulations, revealed the essential influence of rotational and translational motions of particles, especially at lower temperatures, on sintering outcomes. The effect of the orientation of particles on the sintering process was confirmed, with initial configurations markedly determining sintering efficiency and dynamics. Calculated activation energies from this investigation follow those reported in the literature, confirming surface diffusion as the predominant mechanism driving the sintering of Ni NPs.

Aluminium steel clad materials have high potential for industrial applications. Their mechanical properties are governed by an intermetallic layer, which forms upon heat treatment at the Al-Fe interface. Transmission electron microscopy was employed to identify the phases present at the interface by selective area electron diffraction and energy dispersive spectroscopy. Three phases were identified: orthorhombic Al₅Fe₂, monoclinic Al₁₃Fe₄ and cubic Al₁₉Fe₄MnSi₂. An effective interdiffusion coefficient dependent on concentration was determined according to the Boltzmann–Matano method. The highest value of the interdiffusion coefficient was reached at the composition of the intermetallic phases. Afterwards, the process of diffusion considering the evaluated interdiffusion coefficient was simulated using the finite element method. Results of the simulations revealed that growth of the intermetallic phases proceeds preferentially in the direction of aluminium.

A homogenization of billets from Al-Cu-Li-Mg-Sc-Zr alloys should be accomplished at high annealing temperatures exceeding 500 °C. This type of aluminum alloy is susceptible to the depletion of surface layers from Li. Therefore, choosing a suitable homogenization temperature and duration is a crucial step in assuring a homogeneous distribution of alloying elements and optimal exploitation of the potential of the alloy. In situ heating in an electron microscope was performed on a twin-roll-cast Al-Cu-Li-Mg-Sc-Zr alloy to understand the peculiarities of the homogenization process. Four types of primary phase particles rich in Cu, Li, Mg, and Fe were identified in the as-cast material. They appear as coarse particles at the boundaries of eutectic cells. Their partial dissolution occurs at temperatures above 450 °C. They are almost fully dissolved at 550 °C, except for complex phases containing Fe and Cu. Small dimensions of eutectic cells in the range of 10 µm assure a homogeneous distribution of the main alloying elements within the matrix after 20 min of annealing at 530 °C. Direct comparison with the same material prepared by mold casting indicates that such short annealing times result in the dissolution of the main primary phase particles but do not assure a homogeneous distribution of the alloying elements in the whole volume of the specimen.

Thin twin-roll cast strips from a model Al-Cu-Mg-Li-Zr alloy with a small addition of Sc were prepared. A combination of a fast solidification rate and a favorable effect of Sc microalloying refines the grain size and the size of primary phase particles and reduces eutectic cell dimensions to 10–15 $\mathsf{\mu }$m. Long-term homogenization annealings used in conventionally cast materials lasting several tens of hours followed by a necessary dimension reduction through rolling/extruding could be substituted by energy and material-saving procedure. It consists of two-step short annealings at 300 °C/30 min and 450 °C/30 min, followed by the refinement and hardening of the structure using constrained groove pressing. A dense dispersion of 10–20 nm spherical ${\mathrm{Al}}_3(\mathrm{Sc},\mathrm{Zr})$ precipitates intensively forms during this treatment and effectively stabilizes the structure and inhibits the grain growth during subsequent solution treatment at 530 °C/30 min. Small (3%) pre-straining after quenching assures more uniform precipitation of strengthening ${\mathrm{Al}}_2\mathrm{Cu}$ (${\theta }^{\prime }$), ${\mathrm{Al}}_2\mathrm{CuMg}$ ($S\prime$), and Al₂CuLi ($T_1$) particles during subsequent age-hardening annealing at 180 °C/14 h. The material does not contain a directional and anisotropic structure unavoidable in rolled or extruded sheets. The proposed procedure thus represents a model near net shape processing strategy for manufacturing lightweight high-strength sheets for cryogenic applications in aeronautics.