A comparative study of figure-of-merit fiber sensors of the mass concentration of NaCl solutions based on single-mode and multi-mode fibers was carried out. Lossy mode resonance is realized on chemically thinned sections of optical fibers to various diameters (from 26 to 100 μm) coated with ZnTe. Thin-film coatings were applied using the method of metalorganic chemical vapor deposition (MOCVD). Samples of single-mode and multi-mode fiber sensors were created in such a way that the depth and spectral position of resonances in aqueous NaCl solutions coincided. Sensors implemented on a single-mode fiber have a higher sensitivity (5930 nm/refractive index unit (RIU)) compared to those on a multi-mode fiber (4860 nm/RIU) and a smaller half-width of the resonance in the transmission spectrum. According to the results of experiments, figure-of-merit sensors are in the range of refractive indices of 1.33–1.35 for: multi-mode fiber—25 RIU⁻¹, single-mode fiber—75 RIU⁻¹. The sensitivity of the resulting sensors depends on the surface roughness of the ZnTe coating. The roughness of films synthesized on a single-mode fiber is four times higher than this parameter for a coating on a multi-mode fiber. For the first time, in the transmission spectrum during the synthesis of a thin-film coating on a multi-mode fiber, the possibility of separating the first nine orders of resonances into electric and magnetic transverse components has been demonstrated. The characteristics of sensors with the operating wavelength range in the visible (500–750 nm) and infrared (1350–1550 nm) regions of the spectrum are compared. The characteristics of multi-mode lossy mode resonance sensors are demonstrated, which make them more promising for use in applied devices than for laboratory research.

In the presented work, erbium fiber lasers operating in the pulsed mode with a nonlinear element containing a vanadium oxide saturable absorber are demonstrated. The structure of the saturable absorber is based on a segment of thinned silica fiber coated with a thin-film vanadium oxide by the method of metalorganic chemical vapor deposition. A fiber laser scheme is demonstrated that allows controlling the transmission of the internal cavity of the resonator during laser generation and deposition of a thin film. We have demonstrated a method for obtaining and annealing nanocoatings with laser generation control. We controlled the laser output parameters directly during the synthesis of the saturable absorber material. Vanadium oxides obtained in the work demonstrated the Mott–Paierls phase transition practically at room temperature. In this work, the optical characteristics of the output radiation of a fiber laser with a saturable absorber were measured. At temperatures above 70 °C, the coatings demonstrate a passive Q-switch with a repetition rate of 38 kHz and a pulse duration of 3.8 μs. At temperatures below the phase transition, a short-term mode-locking mode occurs. The transmission jump at a wavelength of about 1350 nm during structural rearrangement was 24%. For comparison, VO₂ nanopowder in a polydimethylsiloxane elastomer matrix was used as a saturable absorber material. The nanopowder modulator made it possible to obtain pulses with a frequency of 27 kHz and a duration of about 7.2 μs.

This article describes a study on the synthesis and annealing processes of thin-film coatings of vanadium oxide on flat, parallel substrates made of quartz glass, sapphire, and silicon, as well as optical fibers using an organometallic precursor, triisopropoxy vanadium (V) oxide. For the first time, optical constants of nanomaterials were estimated in real time during synthesis and subsequent annealed using the lossy-mode resonance effect. The coatings produced in an inert atmosphere after deposition were amorphous, comprising a mixture of VO₂, V₂O₅, V₆O₁₃, and V₃O₅. This method allowed for accurate determination of the threshold temperature for the transformation of oxide mixtures into a monocomponent phase. Optimal conditions for synthesis and annealing were determined for the production of vanadium dioxide (VO₂) and pentoxide (V₂O₅). Morphological changes in coated surfaces were observed as a result of heat treatment. The composition and properties of these samples were studied using optical, terahertz and Raman spectroscopy, as well as temperature-dependent analysis of electrical resistance. The morphology of the coating surface was determined using a scanning electron microscope and an atomic force microscope. The reduction of VO_x to VO₂ was studied in an atmosphere of hydrogen and argon during annealing after deposition, with its effectiveness being compared. It was shown for the first time that the reduction of higher vanadium oxides is due to the presence of elemental carbon in the volume of the material formed from a metalorganic precursor during growth of vanadium oxide. Coatings obtained by annealing in hydrogen had a smaller hysteresis loop width (~5 °C) during phase transition compared to coatings obtained by argon annealing (~9 °C). Both types of coatings demonstrated a 50–60% increase in transmission at 1 THz frequency and in the IR region, accompanied by a 10³–10⁴-fold change in electrical resistance.