Aseptic loosening of total joint replacements (TJRs) continues to be the main cause of implant failures. The socioeconomic impact of surgical revisions is hugely significant; in the United Kingdom alone, it is estimated that £135m is spent annually on revision arthroplasties. Enhancing the longevity of titanium implants will help reduce the incidence and overall cost of failed devices. In realising the development of a superior titanium (Ti) technology, we took inspiration from the growing interest in reactive polydopamine thin films for biomaterial surface functionalisations. Adopting a “one-pot” approach, we exposed medical-grade titanium to a mildly alkaline solution of dopamine hydrochloride (DHC) supplemented with (3S)1-fluoro-3-hydroxy-4-(oleoyloxy)butyl-1-phosphonate (FHBP), a phosphatase-resistant analogue of lysophosphatidic acid (LPA). Importantly, LPA and selected LPA analogues like FHBP synergistically cooperate with calcitriol to promote human osteoblast formation and maturation. Herein, we provide evidence that simply immersing Ti in aqueous solutions of DHC-FHBP afforded a surface that was superior to FHBP-Ti at enhancing osteoblast maturation. The facile step we have taken to modify Ti and the biological performance of the final surface finish are appealing properties that may attract the attention of implant manufacturers in the future.

Chitinase 3-like 1, otherwise known as YKL-40, is a secreted glycoprotein purported to have a role in extracellular matrix metabolism. The first mammalian cell type found to express YKL-40 was the human osteosarcoma-derived osteoblast, MG63. In that first study the active vitamin D3 metabolite, 1,25-dihydroxycholecalciferol (1,25D), stimulated YKL-40 expression, thereby indicating that a vital factor for skeletal health promoted YKL-40 synthesis by bone forming cells. However, when these MG63 cells were exposed to 1,25D they were also exposed to serum, a rich source of the pleiotropic lipid mediator, lysophosphatidic acid (LPA). Given that 1,25D is now known to co-operate with selected growth factors, including LPA, to influence human osteoblast differentiation we hypothesised that 1,25D and LPA may work together to stimulate osteoblast YKL-40 expression. Herein we report that 1,25D and LPA synergistically promote YKL-40 expression by MG63 cells. Inhibitors targeting AP1, MEK, Sp1 and STAT3 blunted the expression of both alkaline phosphatase and YKL-40 by MG63 cells in response to co-stimulation with 1,25D and LPA. Other ligands of the vitamin D receptor also co-operated with LPA in driving YKL-40 mobilisation. Collectively our findings highlight another important role of 1,25D and LPA in the regulation of human osteoblast function.

Titanium (Ti) is a widely used material for surgical implants; total joint replacements (TJRs), screws and plates for fixing bones and dental implants are forged from Ti. Whilst Ti integrates well into host tissue approximately 10% of TJRs will fail in the lifetime of the patient through a process known as aseptic loosening. These failures necessitate revision arthroplasties which are more complicated and costly than the initial procedure. Finding ways of enhancing early (osseo)integration of TJRs is therefore highly desirable and continues to represent a research priority in current biomaterial design. One way of realising improvements in implant quality is to coat the Ti surface with small biological agents known to support human osteoblast formation and maturation at Ti surfaces. Lysophosphatidic acid (LPA) and certain LPA analogues offer potential solutions as Ti coatings in reducing aseptic loosening. Herein we present evidence for the successful bio-functionalisation of Ti using LPA. This modified Ti surface heightened the maturation of human osteoblasts, as supported by increased expression of alkaline phosphatase. These functionalised surfaces also deterred the attachment and growth of Staphylococcus aureus, a bacterium often associated with implant failures through sepsis. Collectively we provide evidence for the fabrication of a dual-action Ti surface finish, a highly desirable feature towards the development of next-generation implantable devices.

There is an incentive to functionalise hydroxyapatite (HA) for orthopaedic implant use with bioactive agents to encourage superior integration of the implants into host bone. One such agent is (3S) 1-fluoro-3-hydroxy-4-(oleoyloxy) butyl-1-phosphonate (FHBP), a phosphatase-resistant lysophosphatidic acid (LPA) analogue. We investigated the effect of an FHBP-HA coating on the maturation of human (MG63) osteoblast-like cells. Optimal coating conditions were identified and cell maturation on modified and unmodified, control HA surfaces was assessed. Stress tests were performed to evaluate coating survivorship after exposure to mechanical and thermal insults that are routinely encountered in the clinical environment. MG63 maturation was found to be three times greater on FHBP-modified HA compared to controls (p < 0.0001). There was no significant loss of coating bioactivity after autoclaving (P = 0.9813) although functionality declined by 67% after mechanical cleaning and reuse (p < 0.0001). The bioactivity of modified disks was significantly greater than that of controls following storage for up to six months (p < 0.001). Herein we demonstrate that HA can be functionalised with FHBP in a facile, scalable manner and that this novel surface has the capacity to enhance osteoblast maturation. Improving the biological performance of HA in a bone regenerative setting could be realised through the simple conjugation of bioactive LPA species in the future.