Background: Antimicrobial disinfectants are used as primary treatment options against pathogens on surfaces in healthcare facilities to help prevent healthcare associated infections (HAIs). On many surfaces, pathogenic microorganisms exist as biofilms and form an extracellular matrix that protects them from the antimicrobial effects of disinfectants. Disinfectants are used as all-purpose antimicrobials though very few specifically make biofilm efficacy claims. The objective of this study was to evaluate the efficacy of eight registered disinfectants (six registered by the Environmental Protection Agency and two products registered in by the European Chemical Agency) with general bactericidal claims, but currently no biofilm efficacy claims, againstStaphylococcus aureusATTC-6538 andPseudomonas aeruginosaATCC-15442 biofilms. We hypothesized that hydrogen peroxide and sodium hypochlorite disinfectant products would be more effective than quaternary ammonium chlorides.Methods: This study tested the bactericidal efficacy of eight registered disinfectant products againstS. aureusATCC-6538 andP. aeruginosaATCC-15442 grown on glass coupons using a Center for Disease Control (CDC) biofilm reactor and EPA MLB SOP MB-19. Bactericidal efficacy was determined after treating coupons with disinfectants following standard EPA MLB SOP MB-20.Results: Overall, sodium hypochlorite and hydrogen peroxide disinfectants had significantly higher bactericidal efficacies than quaternary ammonium chloride disinfectants. We also found that all tested disinfectants except for quaternary ammonium chloride disinfectants met and exceeded the EPA standard for bactericidal efficacy against biofilms.Conclusion: In general, bactericidal efficacy against biofilms differed by active ingredient. The efficacies of sodium hypochlorite and hydrogen peroxide disinfectants did not vary between strains, but there were significant differences between strains treated with quaternary ammonium chloride disinfectants.

Background: Disinfectant products are often used on environmental surfaces (e.g. countertops, patient beds) and patient care equipment in healthcare facilities to help prevent the transmission of healthcare-associated infections. Ready-to-use (RTU) disinfectants in the form of pre-wetted towelettes are increasingly popular among healthcare facilities. Currently, the EPA does not require disinfectant manufacturers to include a recommended maximum surface area per towelette on their product labels. The objective of this study was to investigate the efficacy of disinfectant towelette products on a hard non-porous surface across different coverage areas using a quantitative EPA method. We hypothesized that there would be significant differences in the efficacy of disinfectant towelette products, and that the greater surface area(s) wiped would result in reduced bactericidal efficacy. Methods: This study tested ten disinfectant towelette products against Staphylococcus aureus strain ATCC CRM-6538 and Pseudomonas aeruginosa strain ATCC 15442 on Formica surfaces. Defined surface areas were wiped and the towelette weighed before and after wiping to determine the amount of liquid released. Bactericidal efficacy testing was also performed after wiping following standard EPA protocols. Results: We found that disinfectant product, area of surface wiped, and strain impacted the bactericidal efficacy achieved. Disinfectant product type and area of surface wiped significantly impacted the percent of liquid released per ft²from the towelette. Conclusion: Overall, bactericidal efficacy varied by towelette product, surface area wiped, and strain. This study also found that wiping larger surface areas may lead to decreased bactericidal efficacy. Further research is needed to test its implication.

Background: Pre-wetted disinfectant wipes are increasingly being used in healthcare facilities to help address the risk of healthcare associated infections (HAIs). However, HAIs are still a major problem in the US with Clostridioides difficile being the most common cause, leading to approximately 12,800 deaths annually in the US. An underexplored risk when using disinfectant wipes is that they may cross-contaminate uncontaminated surfaces during the wiping process. The objective of this study was to determine the cross-contamination risk that pre-wetted disinfectant towelettes may pose when challenged with C. difficile spores. We hypothesized that although the tested disinfectant wipes had no sporicidal claims, they will reduce spore loads. We also hypothesized that hydrogen peroxide disinfectant towelettes would present a lower cross-contamination risk than quaternary ammonium products. Methods: We evaluated the risk of cross-contamination when disinfectant wipes are challenged with C. difficile ATCC 43598 spores on Formica surfaces. A disinfectant wipe was used to wipe a Formica sheet inoculated with C. difficile. After the wiping process, we determined log₁₀ CFU on previously uncontaminated pre-determined distances from the inoculation point and on the used wipes. Results: We found that the disinfectant wipes transferred C. difficile spores from inoculated surfaces to previously uncontaminated surfaces. We also found that wipes physically removed C. difficile spores and that hydrogen peroxide disinfectants were more sporicidal than the quaternary ammonium disinfectants. Conclusion: Regardless of the product type, all disinfectant wipes had some sporicidal effect but transferred C. difficile spores from contaminated to otherwise previously uncontaminated surfaces. Disinfectant wipes retain C. difficile spores during and after the wiping process.

The objective of this study was to evaluate the extent and potential mechanisms of early onset surface damage from simulated wiping typical of six-months of routine disinfection and to assess the subsequent microbial risk of surfaces damaged by disinfectants. Eight common material surfaces were exposed to three disinfectants and a neutral cleaner (neutral cleaner, quaternary ammonium, hydrogen peroxide, sodium hypochlorite) in accelerated aging tests to simulate a long-term disinfection routine. Materials were also immersed in dilute and concentrated chemical solutions to induce surface damage. Surfaces were chemically and physically characterized to determine extent of surface damage. Bactericidal efficacy testing was performed on the Quat-based disinfectant using a modified version of EPA standard operating procedure MB-25-02. The wiping protocol increased surface roughness for some material surfaces due to mechanical abrasion of the wiping cloth. The increased roughness did not correlate with changes in bactericidal efficacy. Chemical damage was observed for some surface-disinfectant combinations. The greatest observed effects from disinfectant exposure was in changes in wettability or water contact angle. Early onset surface damage was observed in chemical and physical characterization methods. These high-throughput material measurement methods were effective at assessing nanoscale disinfectant-surface compatibility which may go undetected though routine macroscale testing.