Natural rubber is one of the most important renewable biopolymers used in many applications due to its special properties that cannot be easily mimicked by synthetic polymers. To sustain the existence of natural rubber in industries, modifications have been made to its chemical structure from time to time in order to obtain new properties and to enable it to be employed in new applications. The chemical structure of natural rubber can be modified by exposure to ultraviolet light to reduce its molecular weight. Under controlled conditions, the natural rubber chains will be broken by photodegradation to yield low-molecular-weight natural rubber. The aim of this work was to obtain what is known as liquid natural rubber via photodegradation, with titanium dioxide nanocrystals as the catalyst. Titanium dioxide, which was firstly synthesized using the sol–gel method, was confirmed to be in the form of an anatase, with a size of about 10 nm. In this work, the photodegradation was carried out in latex state and yielded low-molecular-weight natural rubber latex of less than 10,000 g/mol. The presence of hydroxyl and carbonyl groups on the liquid natural rubber (LNR) chains was observed, resulting from the breaking of the chains. Scanning electron microscopy of the NR latex particles showed that titanium dioxide nanocrystals were embedded on the latex surface, but then detached during the degradation reaction.

Sintering is a common synthesis method for the fabrication of ceramics. The widespread use of sintering for the production of complex ceramic oxide especially ferrites has led to a variety of investigations on the subject. Top-down approach synthesis like mechanochemical process has recently been suggested as a promising synthesis method for replacing bottom-up approach synthesis methods like sintering, questioning its necessity for thermal treatment at high temperature. Understanding of sintering mechanism is crucial in order to optimize and enhance the advantages of sintering, which cannot be replaced by other techniques. In general, ferrites with particular set of behaviors require a particular set of microstructural properties influenced by the sintering steps. The main objective of this chapter is to understand how the increase of sintering temperature affects the microstructural evolution, in order to develop a fundamental science understanding for the mechanism of sintering. In the second part of this chapter, presentation of experimental results on sintering of mechanically activated Ni0.5Zn0.5Fe2O4 nanoparticles and its effect on microstructural, magnetic, and optical properties was reported. Lastly, a comparative study between sintering (bottom-up approach) and mechanochemical (top-down approach) process is presented.