This research used fly ash and slag to create geopolymer foam concrete. They were activated with an alkali, resulting in a chemical reaction that produced a gel that strengthened the concrete’s structural integrity. The experimental approach involved varying the fly ash content in the precursors at incremental percentages (10%, 30%, 50%, 70% and 90%) and subjecting the fly ash to mechanical activation through a planetary ball mill at distinct rotational speeds (380, 400, 420 and 440 rpm). The investigation discerned that the fly ash content and particle structure exert a discernible influence on macroscopic properties, including flowability, air generation height, compressive strength, dry density and microstructural characteristics such as pore distribution and hydration product arrangement in the geopolymer foam concrete. Employing analytical techniques such as X-ray diffraction (XRD) and scanning electron microscopy (SEM), it was deduced that diminishing the fly ash content correlates with an enhancement in compressive strength. Furthermore, the specific strength of the geopolymer foam concrete reached a peak of 0.041 when the activated fly ash in the planetary ball mill rotated at 420 rpm, manifesting a lightweight and high-strength outcome.

High-Mn twinning-induced plasticity (TWIP) steels are renowned for their exceptional strength-ductility synergy. However, their practical applications are severely constrained by inadequate yield strength and poor corrosion resistance. In this study, an N-alloyed TWIP steel (Fe-25Mn-12Cr-0.3C-0.3N, wt.%, designated as TWIP-2) was developed, using an N-free counterpart (Fe-25Mn-12Cr-0.3C, TWIP-1) as a reference. Both steels underwent hot forging (HF) followed by solution treatment (ST). The synergistic effects of N alloying and thermomechanical processing on the microstructural evolution, mechanical properties, and corrosion behavior were systematically investigated. Results indicate that all samples retain a single-phase FCC austenitic structure. N alloying increased the yield strength of the hot-forged TWIP steel from 488.1 MPa to 802.9 MPa while maintaining an elongation after fracture around 40%. Solution treatment markedly improved corrosion resistance, changing the corrosion mode from intergranular attack to pitting. The TWIP-2-ST specimen exhibited the lowest corrosion current density of 2.88 × 10⁻⁵ A/cm² and demonstrated the best overall performance. This comprehensive improvement in mechanical and corrosion performance is primarily attributed to the elevated work-hardening capacity, a higher fraction of low-energy grain boundaries, and the beneficial role of interstitial N in suppressing pitting nucleation and propagation.