Alkali-activated slag (AAS) is a promising alternative to ordinary Portland cement (OPC) as sole binder for reinforced concrete structures. OPC is reportedly responsible for over 5% of the global CO₂ emission. In addition, slag is an industrial by-product that must be land-filled if not re-used. Therefore, it has been studied by many investigators as environmentally friendly replacement of OPC. In addition to recycling, AAS offers favorable properties to concrete such as rapid development of compressive strength and high resistance to sulfate attack. Some of the potential shortcomings of AAS include high shrinkage, short setting time, and high rate of carbonation. Using ground granulated blast furnace slag (GGBS) as an alternative to OPC requires its activation with high alkalinity compounds such as sodium hydroxide (NaOH), sodium sulfate (Na₂SO₃), sodium carbonate (Na₂CO₃), or combination of these compounds such as NaOH and Na₂SO₃. The mechanism of alkali-activation is still not fully understood and further research is required. This paper overviews the properties, advantages, and potential shortcomings of AAS concrete.

Reducing the environmental footprint of the construction industry in general and concrete in particular is essential. The addition of synthetic and natural fibers to concrete mixes at appropriate dosages enhances durability and strength and extends the lifespan of concrete infrastructures. This study reviews the geometric and mechanical properties of selected fibers such as steel, basalt, polypropylene, polyvinyl alcohol, polyethylene, glass, carbon, and natural fibers and their impact on concrete fresh, mechanical, and durability properties when combined in different configurations. The study focuses on the effect of blending fibers with concrete mixes that use alkali-activated binders based on recycled industrial byproducts such as slag and fly ash and thereby contribute to reduction of CO₂ contribution through complete or partial replacement of Ordinary Portland cement (OPC). As a result, the effect of binder content, binder composition, alkaline activator concentration, and water-to-binder (w/b) ratio on fresh properties, mechanical strength, and durability of concrete with blended fibers is also evaluated in this study. The properties of fiber-reinforced concrete with alkali-activated binder and conventional OPC binders are compared. Fiber-reinforced concrete with alkali-activated binders that are based on industrial byproducts may represent sustainable alternatives to conventional concrete and offers competitive fresh and mechanical properties when fiber properties, fiber content, w/b ratio, binder type, and dosage are carefully considered in concrete mix design.

Reductions of green gas emissions and the reuse/recycling of industrial byproducts are important for the mitigation of the environmental impact of the construction industry. The replacement of ordinary Portland cement (OPC) is a concrete binder with industrial byproducts that possess sufficient cementitious and pozzolanic properties, such as ground granulated blast furnace slag (GBS) and fly ash. This critical review analyzes the effect of some of the most critical parameters on the development of the compressive strength of concrete or mortar that consists of combinations of alkali-activated GBS and fly ash as binders. The review includes the effects of the curing environment, the proportions of GBS and fly ash in the binder, and the concentration of the alkaline activator on strength development. The article also reviews the effect of exposure as well as the age of samples at the time of exposure to acidic media on the development of concrete strength. The effect of acidic media on mechanical properties was found to depend not only on the type of acid but also on the alkaline activator solution, proportions of GBS and fly ash in the binder, and the age of the sample at the time of exposure, among other factors. As a focused review, the article pinpoints important findings such as the change in compressive strength over time when mortar/concrete is cured in an environment that permits the loss of moisture versus curing in a system that retains the alkaline solution and keeps reactants available for hydration and the development of geopolymerization products. The relative contents of slag and fly ash in blended activators have a significant impact on strength development. Research methods used include a critical review of the literature, a comparison of reported research findings, and identifying reasons for agreement or disagreement of findings.

Progressive collapse is one of the most under-researched areas in structural engineering due to the relative scarcity of the circumstances leading to progressive collapse. The current design standards and building codes provide limited prescriptive or performance-based guidance on analysis or design to guard against progressive collapse. The collapse of the World Trade Center on September 11, 2001, led to demands by the public to amend current building codes and provide protection against collapse caused by extreme events. Following September 11, the literature on progressive collapse mitigation has expanded significantly. Important issues examined by investigators include events leading to progressive collapse, assessment of loads, analysis methods, and design philosophy. This paper seeks to explore aspects of the current state of knowledge on progressive collapse in the technical literature. The paper also discusses loads, structural analysis requirements, and design approaches in United States standard...

Reducing the fingerprint of infrastructure has become and is likely to continue to be at the forefront of stakeholders’ interests, including engineers and researchers. It necessary that future buildings produce minimal environmental impact during construction and remain durable for as long as practicably possible. The use of basalt fiber-reinforced polymer (BFRP) bars as a replacement for carbon steel is reviewed in this article by examining the literature from the past two decades with an emphasis on flexural strength, serviceability, and durability. The provisions of selected design and construction guides for flexural members are presented, compared, and discussed. The bond of BFRP bars to the surrounding concrete was reportedly superior to carbon steel when BFRP was helically wrapped and sand coated. Experimental studies confirmed that a bond coefficient k_b = 0.8, which is superior to carbon steel, may be assumed for sand-coated BFRP ribbed bars that are helically wrapped, as opposed to the conservative value of 1.4 suggested by ACI440.1R-15. Code-based models overestimate the cracking load for BFRP-reinforced beams, but they underestimate the ultimate load. Exposure to an alkaline environment at temperatures as high as 60 °C caused a limited reduction in bond strength of BFRP. The durability of BFRP bars is influenced by the type of resin and sizing used to produce the bars.