The triple helix structure of collagen can be degraded by collagenase. In this study, we explored how the intrinsic fluorescence of type I collagen was influenced by collagenase I. We found that tyrosine was the main factor that could successfully excite the collagen fluorescence. Initially, self-assembly behavior of collagen resulted in a large amount of tyrosine wrapped with collagen, which decreased the fluorescence intensity of type I collagen. After collagenase cleavage, some wrapped-tyrosine could be exposed and thereby the intrinsic fluorescence intensity of collagen increased. By observation and analysis, the influence of collagenase to intrinsic fluorescence of collagen was investigated and elaborated. Furthermore, collagenase cleavage to the special triple helix structure of collagen would result in a slight improvement of collagen thermostability, which was explained by the increasing amount of terminal peptides. These results are helpful and effective for reaction mechanism research related to collagen, which can be observed by fluorescent technology. Meantime, the reaction behaviors of both collagenase and collagenolytic proteases can also be analyzed by fluorescent technology. In conclusion, this research provides a foundation for the further investigation of collagen reactions in different areas, such as medicine, nutrition, food and agriculture.

A large amount of cow hair solid waste is produced in leather production, and a reasonable treatment should be developed to reduce the pollution. In this study, cow hair waste was utilized as the carbon precursor, and N₂ was determined to be the most appropriate atmosphere for biochar preparation. We performed a comparison of the properties of biochars that were prepared with different methods, including direct pyrolysis, KOH activation, and the MgO template method. The characterization results show that the highest specific surface area reaches 1753.075 m²/g. Subsequently, the keratin that was extracted from cow hair and purified was used to prepare a biochar with the MgO template method, obtaining an orderly sponge structure. The biochar from cow hair waste was further used to absorb direct blue dye wastewater, and its adsorption capacity reached 1477 mg/g after 10 h with a high efficiency of regeneration. This study successfully utilized keratin-containing hair waste and provides a new source for synthesizing carbon materials for dye wastewater treatment.