9%Ni steel was recently used for the first time in the field of injection unit (IU) for the injection of CO₂ into oil wells. Because such steels are operated in H₂S medium and are susceptible to sulfide stress cracking, their pipes are cladded with Ni-based superalloy 625 by using gas tungsten arc welding with a hot wire to prevent this phenomenon from occurring. The transition zone of substrate/clad can have high hardness and low toughness, and promote failure of the component during service; therefore, it is very important to know its characteristics. In this work, this transition zone was analyzed through optical and scanning electron microscopy with energy dispersive X-ray spectrometry and electron backscatter diffraction, as well as Vickers microhardness, shear and bend tests. Metallographic analysis identified type I and II boundaries with distinct chemical gradients, MC-type carbides, Laves/γ eutectics, peninsulas macrosegregation, crystallographic texture close to in the clads, residual strain, and drop of microhardness across the transition zone. The clads were approved in the shear and bend tests. This work proposes a new type II boundary formation mechanism in dissimilar welds of steels that do not exhibit the allotropic transformation δ → γ during the welding thermal cycle and do not experience a change in the solidification mode.

This work aims to compare the ultrasonic inspection of 9%Ni steel joints welded with the Gas Metal Arc Welding (GMAW) process and Shielded Metal Arc Welding (SMAW) process. These are the two most widely used processes used to weld pipes for CO₂ injection units for floating production storage and offloading (FPSO) in the Brazilian oil and gas industry. The SMAW equipment is simple and portable, which is convenient for the FPSO; however, the GMAW process has the advantage of welding with high productivity. In this study we performed a numerical simulation using the software CIVA, 11th version, to analyze the behavior of ultrasonic longitudinal wave beams through GMAW and SMAW dissimilar weld joints. Ultrasonic tests were performed on calibration blocks drawn from both welded joints to evaluate the simulation results. The results are discussed with regard to the microstructure of the weld metal via electron backscatter diffraction (EBSD) analyses. The SMAW process presented better inspection performance than the GMAW process in terms of attenuation and dispersion effects. Although the SMAW had a better outcome, for both processes the configuration of 16 active elements and a scanning angle of 48° resulted in an optimized inspection of the entire joint.

The ultrasonic inspection of thick-walled welded joint with austenitic weld metal has proven to be a challenge due to its anisotropic microstructure that can promote ultrasonic waves attenuation. This work aimed to optimize the phased array ultrasonic inspection of the thick-walled joint of a 9% Ni steel pipe welded with Ni-based superalloy 625. The development was carried out by CIVA numeric simulation to preview the beam behavior during the inspection of GTAW (Gas Tungsten Arc Welding)/SMAW (Shielded Metal Arc Welding) joint with anisotropic weld metal. To validate the simulation results, experimental tests were performed with a phased array transducer using longitudinal waves on a calibration block withdrawn from the joint. The configuration of low frequency (2.25 MHz), 16 active elements and a scanning angle of 48° ensured the inspection of the entire joint and the computational simulation proved to be essential for the success of the inspection.