Introducing fire-retardant additives or building blocks into resins is a widely adopted method used for improving the fire retardancy of epoxy composites. However, the increase in viscosity and the presence of insoluble additives accompanied by resin modification remain challenges for resin transfer molding (RTM) processing. We developed a robust approach for fabricating self-extinguishing RTM composites using unmodified and flammable resins. To avoid the effects on resin fluidity and processing, we loaded the flame retardant into tackifiers instead of resins. We found that the halogen-free flame retardant, a microencapsulated red phosphorus (MRP) additive, was enriched on fabric surfaces, which endowed the composites with excellent fire retardancy. The composites showed a 79.2% increase in the limiting oxygen index, a 29.2% reduction in heat release during combustion, and could self-extinguish within two seconds after ignition. Almost no effect on the mechanical properties was observed. This approach is simple, inexpensive, and basically applicable to all resins for fabricating RTM composites. This approach adapts insoluble flame retardants to RTM processing. We envision that this approach could be extended to load other functions (radar absorbing, conductivity, etc.) into RTM composites, broadening the application of RTM processing in the field of advanced functional materials.

The nanocomposites with reversible cross-linking covalent bonds were prepared by reacting furfurylamine (FA)-modified diglycidyl ether of bisphenol A (DGEBA) and furfuryl-functionalized aniline trimer-modified graphene (TFAT-G) with bismaleimide (BMI) via the Diels-Alder (DA) reaction. The successful synthesis of the TFAT modifier is confirmed by nuclear magnetic resonance (NMR) hydrogen spectroscopy and IR spectroscopy tests. The structure and properties of TFAT-G epoxy nanocomposites are characterized by scanning electron microscopy (SEM), differential scanning calorimeter (DSC), tensile, and resistivity. The results show that TFAT-G was uniformly dispersed in the resin, and 1 wt% TFAT-G composites increased to 233% for tensile strength, 63% for elongation at break, 66% for modulus, and 7.8 °C for Tg. In addition, the addition of unmodified graphene degrades the mechanical properties of the composite. Overall, the graphene/self-healing resin nanocomposites have both good self-healing function and electrical conductivity by adding 1 wt% modified graphene; this allows for the maintenance of the original 83% strength and 89% electrical conductivity after one cycle of heating repair.

In this paper, interlayer toughening composites were prepared by the z-directional injection RTM process (z-RTM), which has the advantage of increasing the interlaminar toughness and shortening the filling time and completely impregnating the fibers. The nonwoven fabrics and dot matrix structure material were used as ex situ interlayer toughening agents. The effect of the interlayer toughening agent structure on the resin flow behavior during the z-RTM process was investigated. The macro-flowing and micro-infiltration behaviors of the resin inside the preforms were deduced. The permeability of the fabric preforms with different toughening agents was investigated. The results show that the introduction of the nonwoven structure toughening agent makes the macro flow slow, and the flow front more uniform. The toughening agent with a dot matrix structure promotes the resin macro flow in the preforms, and shortens the injection time. The z-directional permeability of the preform with a dot matrix structural toughening agent is one order of magnitude lower than that of the non-toughened preform, while being higher than the preform toughened by the nonwoven fabric preforms, which is helpful for the further applicability of the z-RTM process. Furthermore, the mode II interlaminar fracture toughness of composites was evaluated.

The nanocomposites with reversible cross-linking covalent bonds were prepared by reacting furfurylamine (FA)-modified diglycidyl ether of bisphenol A (DGEBA) and furfuryl-functionalized aniline trimer-modified graphene (TFAT-G) with bismaleimide (BMI) via Diels-Alder (DA) reaction. The successful synthesis of the TFAT modifier is confirmed by NMR hydrogen spectroscopy and IR spectroscopy tests. The structure and properties of TFAT-G epoxy nanocomposites are characterized by SEM, DSC, tensile and resistivity CES. The results show that TFAT-G was uniformly dispersed in the resin, and 1wt% TFAT-G composites increase to 233% for tensile strength, 63% for elongation at break, 66.1% for modulus and 7.8℃ for Tg. Overall, the graphene/self-healing resin nanocomposites have both good self-healing function and electrical conductivity by adding 1% modified graphene and still maintain the original 83% strength and 89% electrical conductivity after one cycle of heating repair.