The advancement of aerospace, marine engineering, and advanced energy systems hinges on material performance under extreme service conditions (intense thermal exposure, severe corrosion, high mechanical stress)

In this paper, a series of Co-free FeCr_0.6Ni_0.6(AlSi)_x (x = 0, 0.1, 0.12, 0.14, 0.16) high-entropy alloys (HEAs) were designed and fabricated by suction casting, and the effects of equi-molar (Al, Si) co-addition in these Fe-rich Fe-Cr-Ni-based HEAs on microstructure, mechanical properties, and corrosion resistance were systematically investigated. It is found that equi-molar (Al, Si) co-addition could cause the phase formation from FCC to FCC + BCC, while the morphologies of the phases change from dendrite-type to sideplate-type. Moreover, trade-off between strength and plasticity occurs with the increase in (Al, Si) co-addition, and the production of ultimate tensile strength and plasticity reaches the highest value when x = 0.12, while there exists a narrow region for x values to realize excellent comprehensive mechanical properties. In addition, similar corrosion resistance in 3.5 wt.% NaCl solution higher than 316L stainless steel could be realized in the HEAs with x = 0.12 and 0.14, while the latter one is slightly lower in pitting corrosion and the width of passive region, which is possibly caused by the increase in the density of phase boundaries. This work provides a novel insight on designing high-performance cost-effective Fe-rich and (Al, Si)-containing (Fe-Cr-Ni)-based HEAs combining high mechanical properties and corrosion resistance.

CoCrNiTiAl_x high-entropy alloy films with varied Al contents were fabricated on 42CrMo steel substrates via magnetron sputtering. By adjusting the sputtering power of the Al target, an investigation was systematically carried out to explore the effect of different Al contents on the microstructural evolution, mechanical properties, and corrosion resistance of the film, with the underlying synergistic mechanism governing these properties being elucidated. With increasing Al content, the film microstructure gradually transforms from an amorphous phase at low Al contents to a nanocrystalline–amorphous composite structure, until it is converted into the BCC phase, and the film’s crystallinity exhibits a trend of first increasing and then decreasing. In terms of mechanical properties, the film hardness is significantly enhanced from 7.6 ± 1.3 GPa to 18.9 ± 1.1 GPa with increasing Al content, while the toughness gradually declines. Wear tests show that the film wear rate first decreases and then increases with rising Al content, reaching a minimum of 2.06 × 10⁻⁵ mm³/N·m. The superior protective state, characterized by a corrosion potential reaching −361.2 mV and corrosion current density dropping to 1.12 μA/cm², arises from the generation of an integrated, consistently structured composite passivation barrier in 3.5 wt.% solution. This study confirms that appropriate Al doping can synergistically optimize the microstructure, mechanical properties, and corrosion resistance of CoCrNiTiAl_x films, providing experimental and theoretical support for the compositional design and engineering applications of high-performance high-entropy alloy protective films.