Solidification of cathode ray tube (CRT) panel glass was carried out using a hydrothermal processing method. In this way, the glass powder was first compacted in a mold at 20 MPa, and then hydrothermally cured in an autoclave under saturated steam pressure at 200 ℃ for 6 hours. The CRT panel glass was then hydrothermally solidified by the formation of tobermorite (Ca₅Si₆O₁₆(OH)₂·4H₂O), which was encouraged by the addition of slaked lime (Ca(OH)₂). The final solidified specimen’s strength was heavily depended on the amount of tobermorite formed, with higher concentrations of tobermorite producing commensurately greater mechanical strength. With the addition of slaked lime at 20%-30% by mass, the specimen achieved a flexural strength of approximately 16 MPa, which is sufficiently great for using as a construction material. As such, there is cause to believe that the hydrothermal processing method used here may have substantial potential for the product of high-quality recycled CRT panel glass with properties suitable for utilization as a construction material.