A mixed metal oxide W-TiO₂ nanopowder photocatalyst was prepared by using the sol–gel method with a broad range of elemental compositions x = C_W/(C_W + C_Ti), including TiO₂ and WO₃. The material was structurally characterized and evaluated in adsorption and photocatalytic processes by testing its removal capacity of a representative pollutant methylene blue (MB) in aqueous solutions and under UV-A and sunlight illuminations. The nanopowders appeared to be more effective adsorbents than pure TiO₂ and WO₃ materials, showing a maximum at 15 mol% W, which was set as the tungsten solubility limit in anatase titania. At the same time, the photocatalytic decomposition of MB peaked at 2 mol% W. The examination of different compositions showed that the most effective MB removal took place at 15 mol% W, which was attributed to the combined action of adsorption and heterogeneous photocatalysis. Moreover, MB decomposition under sunlight was stronger than under UV-A, suggesting photocatalyst activation by visible light. The pollutant removal efficiency of the material with 15 mol% W was enhanced by a factor of ~10 compared to pure TiO₂ at the beginning of the process, which shows its high potential for use in depollution processes in emergency cases of a great pollutant leak. As a result, a W_x=0.15-TiO₂ catalyst could be of high interest for wastewater purification in industrial plants.

Cu–TiO₂ nanoparticles of a broad range of compositions with 0, 0.002, 0.005, 0.02, 0.05, 0.2, 0.5, 1.0, 2.0, 3.0, 5.0, 7.0 and 10.0 mol% Cu were synthesized via the sol–gel method using copper (II) acetate and titanium tetraisopropoxide (TTIP) precursors at a low hydrolysis ratio of H = 1.25, which favours homogeneous TiO₂ nucleation and Cu dispersion in the host matrix at nanoscale. The precipitated materials were dried at 80 °C and calcined at 450, 500, and 550 °C to form crystalline nanopowders, whose photocatalytic activity was evaluated on the decomposition of a representative pollutant, methylene blue (MB), in aqueous solutions under UVA and sunlight illuminations. The compositions with small Cu content of ~0.05 mol% showed the highest activity. A gain of activity over pure titania of 4 times after calcination at 450 °C, 2.5 times at 500 °C and 20% at 550 °C was measured under UVA illumination. Even higher gain of activity observed under sunlight illumination might be due to an extension of action spectrum to the visible range due to intra-gap defect states produced by Cu²⁺ insertion. The time-resolved microwave conductivity (TRMC) measurements of the photoinduced charges relaxation suggest that both excessive calcination temperature and Cu content decrease the activity due to Cu-defects clustering. Modelling relates the activity to the photoinduced electron-hole pair separation; the optimal Cu content is explained by accessibility of the recombination centre by a conduction band (CB) electron. Accordingly, an increase in calcination temperature resulted in a longer pathlength of CB electron.