An approach for the size measurement of particulate (nano)materials by transmission electron microscopy was evaluated. The approach combines standard operating procedures for specimen preparation, imaging, and image analysis, and it was evaluated on a series of certified reference materials and representative test materials with varying physical properties, including particle size, shape, and agglomeration state. The measurement of the median value of the minimal external particle diameter distribution was intra-laboratory validated. The validation study included an assessment of the limit of detection, working range, selectivity, precision, trueness, robustness, and ruggedness. An uncertainty that was associated to intermediate precision in the range of 1–7% and an expanded measurement uncertainty in the range of 7–20% were obtained, depending on the material and image analysis mode. No bias was observed when assessing the trueness of the approach on the certified reference materials ERM-FD100 and ERM-FD304. The image analysis method was validated in an inter-laboratory study by 19 laboratories, which resulted in a within-laboratory precision in the range of 2–8% and a between-laboratory precision of between 2% and 14%. The automation and standardization of the proposed approach significantly improves labour and cost efficiency for the accurate and precise size measurement of the particulate materials. The approach is shown to be implementable in many other electron microscopy laboratories.

E171 (titanium dioxide) is a food additive that has been authorized for use as a food colorant in the European Union. The application of E171 in food has become an issue of debate, since there are indications that it may alter the intestinal barrier. This work applied standardized and validated methodologies to characterize representative samples of 15 pristine E171 materials based on transmission electron microscopy (TEM) and single-particle inductively coupled plasma mass spectrometry (spICP-MS). The evaluation of selected sample preparation protocols allowed identifying and optimizing the critical factors that determine the measurement of the particle size distribution by TEM. By combining optimized sample preparation with method validation, a significant variation in the particle size and shape distributions, the crystallographic structure (rutile versus anatase), and the physicochemical form (pearlescent pigments versus anatase and rutile E171) was demonstrated among the representative samples. These results are important for risk assessment of the E171 food additive and can contribute to the implementation of the European Food Safety Authority (EFSA) guidance on risk assessment of the application of nanoscience and nanotechnologies in the food and feed chain.

In single particle inductively coupled plasma mass spectrometry (spICP-MS), the transport efficiency is fundamental for the correct determination of both particle number concentration and size. In the present study, transport efficiency was systematically determined on three different days with six carefully characterised gold nanoparticle (AuNP) suspensions and in seven European and US expert laboratories using different ICP-MS instruments and spICP-MS software. Both particle size—(TES)—and particle frequency—(TEF)—methods were applied. The resulting transport efficiencies did not deviate much under ideal conditions. The TEF method however systematically resulted in lower transport efficiencies. The extent of this difference (0–300% rel. difference) depended largely on the choice and storage conditions of the nanoparticle suspensions used for the determination. The TES method is recommended when the principal measurement objective is particle size. If the main aim of the measurement is the determination of the particle number concentration, the TEF approach could be preferred as it might better account for particle losses in the sample introduction system.

E174 (silver) is a food additive that may contain silver nanoparticles (AgNP). Validated methods are needed to size and quantify these particles in a regulatory context. However, no validations have yet been performed with food additives or real samples containing food additives requiring a sample preparation step prior to analysis. A single-particle inductively coupled plasma mass spectrometry (spICP-MS) method was developed and validated for sizing and quantifying the fraction of AgNP in E174 and in products containing E174, and associated uncertainties related to sample preparation, analysis and data interpretation were unraveled. The expanded measurement uncertainty for AgNP sizing was calculated to be 16% in E174-containing food products and increased up to 23% in E174 itself. The E174 food additives showed a large silver background concentration combined with a relatively low number of nanoparticles, making data interpretation more challenging than in the products. The standard uncertainties related to sample preparation, analysis, and challenging data interpretation were respectively 4.7%, 6.5%, and 6.0% for triplicate performances. For a single replicate sample, the uncertainty related to sample preparation increased to 6.8%. The expanded measurement uncertainty related to the concentration determination was 25–45% in these complex samples, without a clear distinction between additives and products. Overall, the validation parameters obtained for spICP-MS seem to be fit for the purpose of characterizing AgNP in E174 or E174-containing products.

Silver (E174) is authorised as a food additive in the EU. The unknown particle size distribution of E174 is a specific concern for the E174 risk assessment. This study characterised the fraction of silver (nano)particles in 10 commercially available pristine E174 food additives and 10 E174-containing products by transmission electron microscopy (TEM) and single-particle inductively coupled plasma-mass spectrometry (spICP-MS). TEM analysis showed that all samples contained micrometre-sized flakes and also a fraction of (nano)particles. Energy-dispersive X-ray spectroscopy (EDX) and electron diffraction confirmed that the (nano)particles and micrometre-sized flakes consisted of silver. A higher amount of (nano)particles was observed in the products than in the food additives. In addition, the surface of the micrometre-sized flakes was rougher in products. The median of the minimum external dimension, assessed as minimal Feret diameter, of the fraction of (nano)particles determined by quantitative TEM analysis was 11 ± 4 nm and 18 ± 7 nm (overall mean ± standard deviation), for food additives and products, respectively. Similar size distributions were obtained by spICP-MS and TEM, considering the limit of detection of spICP-MS. The median of the equivalent spherical diameter of the fraction of (nano)particles determined by spICP-MS was 19 ± 4 nm and 21 ± 2 nm (overall mean ± standard deviation), for food additives and products, respectively. In all samples, independent of the choice of technique, the nano-sized particles represented more than 97% (by number) of the silver particles, even though the largest mass of silver was present as flakes. GRAPHICAL ABSTRACT

Silver-based biocides are applied in face masks because of their antimicrobial properties. The added value of biocidal silver treatment of face masks to control SARS-CoV-2 infection needs to be balanced against possible toxicity due to inhalation exposure. Direct measurement of silver (particle) release to estimate exposure is problematic. Therefore, this study optimized methodologies to characterize silver-based biocides directly in the face masks, by measuring their total silver content using ICP-MS and ICP-OES based methods, and by visualizing the type(s) and localization of silver-based biocides using electron microscopy based methods. Thirteen of 20 selected masks intended for general use contained detectable amounts of silver ranging from 3 μg to 235 mg. Four of these masks contained silver nanoparticles, of which one mask was silver coated. Comparison of the silver content with limit values derived from existing inhalation exposure limits for both silver ions and silver nanoparticles allowed to differentiate safe face masks from face masks that require a more extensive safety assessment. These findings urge for in depth characterization of the applications of silver-based biocides and for the implementation of regulatory standards, quality control and product development based on the safe-by-design principle for nanotechnology applications in face masks in general.