Addressing the limitations of poor piezoelectric photocatalytic activity and insufficient magnetic recovery in pure BiFeO3 nanoparticles, Gd and Zr co-doped BiFeO3 nanoparticles were synthesized via the sol-gel method. The structural characterization revealed a rhombohedral-to-orthorhombic phase transition with reduced grain size (~35 nm) and lattice distortion due to dopant incorporation. An XPS analysis confirmed Fe3+ dominance and oxygen vacancy enrichment, while optimized BGFZ9 exhibited enhanced remanent magnetization (0.1753 emu/g, 14.14 increase) compared to undoped BFO. The synergistic piezo-photocatalytic system achieved 81.08% Ofloxacin degradation within 120 min (rate constant: 0.0136 min−1, 1.26 higher than BFO) through stress-induced piezoelectric fields that promoted electron transfer for ·O2−/·OH radical generation via O2 reduction. The Ofloxacin degradation efficiency decreased to 24.36% after four cycles, with structural integrity confirmed by XRD phase stability. This work demonstrates a triple-optimization mechanism (crystal phase engineering, defect modulation, and magnetic enhancement) for designing magnetically recoverable multiferroic catalysts in pharmaceutical wastewater treatment.

A single crystal with nominal composition Pb(Mg_1/3Nb_2/3)O₃-32PbTiO₃ (PMN-32PT) was grown by the Bridgman technique. Crystal orientation was determined using the rotating orientation X-ray diffraction (RO-XRD). Element distribution was measured along different directions using inductively coupled plasma-mass spectrometry (ICP-MS). The effect of the element segregation along axial and radial directions on the electrical properties of the PMN-32PT crystal was investigated. It is indicated that the electrical properties of the samples along the axial direction were strongly dependent on the PT (PbTiO₃) content. With the increase of the PT content, the piezoelectric coefficient and remnant polarization were improved. Differently, the electrical properties of the samples along the radial direction were mainly determined by the ratio of the Nb and Mg. The reasons for the element segregation and electrical properties varied with the composition were discussed.