There is an increasing demand for ultrasound imaging technologies, particularly wearable and portable systems, for continuous physiological monitoring applications. Although some recent flexible ultrasound devices have adopted polymer encapsulations, typical rigid transducer designs still include metal housings and costly electrodes, contributing to increased device weight and fabrication cost. To address these limitations, we developed an aluminum-electrode/3D-printed polymer-housing ultrasound transducer (APUT) utilizing a polyvinylidene fluoride piezoelectric film. Compared to a gold-electrode/metal-housing ultrasound transducer, the APUT material costs and total weight were approximately 66% and 86% lower, respectively. Acoustic evaluation revealed a center frequency of 24.5 MHz and a fractional bandwidth of 60.9%, with axial and lateral resolutions of 51 and 152 μm, respectively. Furthermore, during a 3-h pulsed operation test, the APUT exhibited an initial increase in capacitance followed by a relatively stable response, with no progressive surface-temperature increase detected within the accuracy of the measurement method. Finally, successful ex vivo imaging of chicken breast tissue confirms the APUT’s biomedical applicability, highlighting its potential as a wearable, portable, and disposable ultrasound platform.

Temperature-dependent characterization of nanomaterials is commonly performed through electrical measurements, and many temperature-sensing applications similarly rely on electrical readout signals. Although these approaches are simple and widely used, they require direct sample contact and may lose sensitivity when the electrical response is weak, saturated, or only weakly dependent on temperature. In this study, a photoacoustic (PA) measurement system was used to evaluate the temperature-dependent response of AgNW networks. PA measurement system detects ultrasonic waves generated through transient thermoelastic expansion after optical absorption, which enables sensitive probing of temperature-dependent optothermal responses beyond conventional electrical measurements. Silver nanowire (AgNW) films with different surface coverage were fabricated through one to four repeated spin-coating cycles using a 1% AgNW ethanol dispersion containing nanowires with diameters of 20–40 nm and lengths of 10–20 µm. The photoacoustic (PA) signals of the fabricated films were measured at various temperatures using a customized PA measurement system and were compared with sheet resistance values obtained using a four-point probe. Both sheet resistance and PA signals increased with increasing temperature, regardless of AgNW surface coverage. Notably, AgNW films with higher surface coverages showed only weak temperature dependence in sheet resistance but pronounced temperature-dependent PA response. These results indicate that PA analysis is particularly useful for characterizing AgNW networks with higher surface coverage, including those used in stretchable electrodes. All samples showed linear relationships for both sheet resistance and PA signals, with coefficients of determination (R²) exceeding 0.9. Overall, these findings suggest that PA measurement may provide complementary information on temperature-dependent behavior that is not fully reflected in sheet-resistance measurements.