In this work, hybrid gliadin electrospun fibers containing inclusion complexes of ferulic acid (FA) with hydroxypropyl-beta-cyclodextrins (FA/HP-β-CD-IC) were prepared as a strategy to increase the stability and solubility of the antioxidant FA. Inclusion complex formation between FA and HP-β-CD was confirmed by Fourier transform infrared spectroscopy (FTIR), differential scanning calorimeter (DSC), and X-ray diffraction (XRD). After adjusting the electrospinning conditions, beaded-free fibers of gliadin incorporating FA/HP-β-CD-IC with average fiber diameters ranging from 269.91 ± 73.53 to 271.68 ± 72.76 nm were obtained. Control gliadin fibers containing free FA were also produced for comparison purposes. The incorporation of FA within the cyclodextrin molecules resulted in increased thermal stability of the antioxidant compound. Moreover, formation of the inclusion complexes also enhanced the FA photostability, as after exposing the electrospun fibers to UV light during 60 min, photodegradation of the compound was reduced in more than 30%. Moreover, a slower degradation rate was also observed when compared to the fibers containing the free FA. Results from the release into two food simulants (ethanol 10% and acetic acid 3%) and PBS also demonstrated that the formation of the inclusion complexes successfully resulted in improved solubility, as reflected from the faster and greater release of the compounds in the three assayed media. Moreover, in both types of hybrid fibers, the antioxidant capacity of FA was kept, thus confirming the suitability of electrospinning for the encapsulation of sensitive compounds, giving raise to nanostructures with potential as active packaging structures or delivery systems of use in pharmaceutical or biomedical applications.

This paper presents a comprehensive study on the electrohydrodynamic processing of gliadin to develop food-grade delivery systems with different morphologies. The effects of biopolymer concentration, applied voltage and solution flow-rate on particle morphology, molecular organisation, crystallinity and thermal properties were investigated. Gliadin concentration influenced the apparent viscosity and conductivity of the solutions, giving raise to particle morphologies at 10 wt% gliadin and beaded-free fibers above 25 wt% gliadin. In general, increasing the voltage resulted in smaller average sizes of the obtained structures, while no significant differences in morphology were observed among the tested flow rates. Interestingly, the amide I position in the FTIR reflected changes in protein conformation which could be correlated with the final morphology attained. Moreover, the acetic acid used for solution preparation disrupted the original amino acid chain packing of the gliadin fraction, being the electrospun/electrosprayed samples amorphous. These gliadin-based microparticles and microfibers obtained could serve as food-grade delivery vehicles.