The components of OLED encapsulation with hermetic sealing and a 1026-day lifetime were measured by PXI-1033. The optimal characteristics were obtained when the thickness of the TPBi layer was 20 nm. This OLED obtained a maximum luminance (Lmax) of 25,849 cd/m² at a current density of 1242 mA/cm², an external quantum efficiency (EQE) of 2.28%, a current efficiency (CE) of 7.20 cd/A, and a power efficiency (PE) of 5.28 lm/W. The efficiency was enhanced by Lmax 17.2%/EQE 0.89%/CE 42.1%/PE 41.9%. The CIE coordinates of 0.32, 0.54 were all green OLED elements with wavelengths of 532 nm. The shear strain and leakage test gave results of 16 kgf and 8.92 × 10⁻⁹ mbar/s, respectively. The reliability test showed that the standard of MIL-STD-883 was obtained.

A multimode waveguide interference (MMI) coupler is combined with a critical linear tapered waveguide on a silicon-on-insulator (SOI) chip. When the TE₀ mode is a critical adiabatic mode conversion from a single-mode waveguide to an extreme linear tapered waveguide combined with an MMI, this linear tapered waveguide is achieved to the maximum divergence angle (i.e., the shortest length). The maximum divergence angle is expressed by θ ≤ 2 tan⁻¹[(0.35W_mmi − W_s)/(0.172L_mmi)] under a 1 × 1 MMI combined with this critical linear tapered waveguide. The expression formula is demonstrated by three different widths of a 1 × 1 MMI of 4 μm/8 μm/12 μm combined with the critical linear tapered waveguide. So, the maximum divergence angle is obtained at θ = 16°/14°/8°, with respect to this linear tapered waveguide loss of 0.022 dB/0.172 dB/0.158 dB, and this linear tapper length is reduced by 93.7%/92.9%/87.5% than the divergence angle θ = 1°. The output power of a 1 × 1 MMI combined with a critical linear tapered waveguide is enhanced at least 1.5 times under 0.95 above condition.