Hierarchically porous monolithic materials are advantageous as adsorbents, catalysts and catalyst supports due to the better accessibility of reactants to the active sites and the ease of recycle and reuse. Traditional synthetic routes, however, have limitations in designing hierarchical porosity as well as the mechanically stable monolithic shape in inorganic phosphate materials, which are useful as adsorbents and catalysts. We present a low-temperature, one-step liquid phase synthesis of hierarchically porous zirconium phosphate (ZrP) monoliths with tunable compositions (from Zr(HPO₄)₂ (Zr : P = 1 : 2) to NaSICON (Na super ionic conductor)-type ZrP (Zr : P = 1 : 1.5)) as well as macropore size (from 0.5 to 5 μm). The as-synthesized ZrP monolith with a high reactive surface area (600 m² g⁻¹) and relatively high mechanical strength (Young's modulus 320 MPa) was applied to ion adsorption. A simple syringe device inserted tightly with the ZrP monolith as a continuous flow setup was demonstrated to remove various toxic metal ions in aqueous solutions, which shows promising results for water purification.

The ingestion of fluoride-contaminated water causes serious health issues in people all over the world. In the current study, the adsorption of fluoride onto chicken bone char (CBC) was investigated as a defluoridation technique. Finer-sized CBC with a diameter of 106–212 µm was used to investigate the fluoride adsorption capacity onto CBC. Results revealed that finer-sized CBC yielded an unusually high fluoride adsorption capacity of 11.2 mg/g at the equilibrium fluoride concentration of 10 mg/L. The study shows that CBC can be utilized in the defluoridation of drinking water and that finer-sized CBC enhances ion exchange to perform a higher adsorption capacity.