Medial proximal sesamoid bones (PSBs) from Thoroughbred racehorses that did (Case) or did not (Control) experience unilateral biaxial PSB fracture were evaluated for bone volume fraction (BVF), apparent mineral density (AMD), tissue mineral density (TMD), and microdamage in Case fractured, Case contralateral limb intact, and Control bones. A majority of Case bones had a subchondral lesion with high microdamage density, and low BVF, AMD, and TMD. Lesion microdamage and densitometric measures were associated with training history by robust linear regression. Exercise intensity was negatively related to BVF (0.07 ≤ R² ≤ 0.12) and positively related to microcrack areal density (0.21 ≤ R² ≤ 0.29) in the lesion; however, in an undamaged site, the relationships were opposite in direction. Regardless of location, TMD decreased with event frequency for both Case and Control, suggesting increased bone remodeling with exercise. Measures of how often animals were removed from active training (layups) predicted a decrease in TMD, AMD, BVF, and microdamage at regions away from the lesion site. A steady‐state compartment model was used to organize the differences in the correlations between variables within the data set. The overall conclusions are that at the osteopenic lesion site, repair of microdamage by remodeling was not successful (e.g., lower bone mass, increased damage, and lower mineralization) but that in regions away from the lesion remodeling successfully controlled damage (e.g., higher bone mass, less microdamage, and lower mineralization).

This study is the first biomechanical research of headless compression screws for fixation of vertical shear fractures of the medial malleolus, a promising alternative that potentially offers several advantages for fixation.Vertical shear fractures were simulated by osteotomies in 20 synthetic distal tibiae. Models were randomly assigned to fixation with either 2 parallel

Shoulder arthroplasty is becoming increasingly common. With evolving implant designs, multiple humeral stem options exist for the surgeon to choose from. New stemless and short-stem systems are modular, remove less native bone stock, and better adapt to patient anatomy. It has been suggested that shorter stem implants may be protective against periprosthetic fracture; however, this has not been mechanistically evaluated. Therefore, this study aimed to biomechanically test synthetic humeri with long-stem, short-stem, and stemless arthroplasty components in a torsional manner to evaluate their response to loading and characterize failure. Twenty-four synthetic humeri were implanted with long stem, short stem, or stemless uncemented prosthesis, 8 in each group. Humeri were mounted in a custom testing jig with a morse taper interfacing with a mechanical testing system. After a 20N axial force, specimens were torsionally loaded to failure at 15 degrees/sec, with 50 Hz collection. Torque vs. rotation curves were generated for each specimen, and stiffness, yield, ultimate strength, and failure load were measured. ANOVA and post hoc pairwise comparisons were used to assess effect of stem type on mechanical test variable. The association of the stem type with fracture type was analyzed by a Fisher’s Exact test. Statistical significance was set at P < .05. During torsional loading, long-stem implants were significantly stiffer than short or stemless implants. The angle of implant yielding was similar across stem designs; however, stemless implants had a lower yield torque. This correlated with a decreased yield energy in stemless compared to short stems as well. Maximum torque and failure torque was also significantly higher in short-stem and long-stem implants compared to stemless. Periprosthetic fractures in shoulder arthroplasty are a concern in low-energy trauma, and stem design likely plays a significant role in early implant-bone failure. Our results suggest stemless implants under torsional load fail at lower stress and are less stiff than stemmed implants. The failure mechanism of stemless implants through metaphyseal cancellous bone emphasizes the effect bone quality has on implant fixation. There is likely a balance of torsional stability to survive physiologic loads while minimizing diaphyseal stress and risk of diaphyseal periprosthetic fracture. This combined with revision and fixation options represent decisions the surgeon is faced with when performing shoulder arthroplasty.