There is an increasing global trend to find sustainable, environmentally friendly and cost-effective materials as an alternative to limited natural raw materials. Similarly, the use of waste materials has been gaining popularity in the production of hot-mix asphalt (HMA). In this study, the sustainable use of glass-fiber-reinforced polyester (GRP) pipe waste powder (GRP-WP), gathered from the cutting and milling process of GRP pipe production, utilizing it in asphalt mixes as a filler, is evaluated based on lab testing to find out: (i) if it produces similar or better performance compared to the most conventionally available filler material (limestone) and, (ii) if so, what would be the optimum GRP-WP filler content to be used in asphalt mixes. For this reason, an experimental test matrix consisting of 45 samples with three different amounts of binder content (4%, 4.5% and 5.0%), and a 5% filler content with five different percentages of the GRP-WP content (0%, 25%, 50%, 75% and 100% replacement by weight of the filler), was prepared to figure out which sample would produce the similar Marshall stability and flow values compared to the control samples while also satisfying specification limits. It was found that the samples with 4.5% binder content, 3.75% GRP-WP and 1.25% limestone filler content produced the results both satisfying the specification requirements and providing an optimum mix design. It is believed that use of GRP-WP waste in HMA production would be a very useful way of recycling GRP-WP.

Bu çalışmada ferrokrom tesislerinde kromit cevherinin zenginleştirilmesi sürecinde ortaya çıkan atık olivin malzemesinin esnek üstyapılarda filler olarak kullanılabilirliği araştırılmıştır. İlk aşamada geleneksel kırmataş kalker agregası tozu kullanılarak elde edilen gradasyonda sabit filler oranı %4.7 olarak alınmış ve bitüm oranı %3,5, %4,0, %4,5, %5,0, %5,5 alınarak optimum bitüm yüzdesi elde edilmiştir. İkinci aşamada, ilk aşamada bulunan optimum bitüm yüzdesi ile geleneksel kırmataş kalker agregası tozuna %0, %25, %50, %75 ve %100 oranlarında olivin ikame edilerek oluşturulan numunelere; stabilite, akma, pratik özgül ağırlık, boşluk yüzdesi, asfalt dolu boşluk yüzdesi ve agregalar arası boşluk yüzdesi deneyi yapılmıştır. Elde edilen sonuçlara göre geleneksel kırmataş kalker agregası filler malzemesiyle ikame edilen olivin yüzdelerine göre asfalt betonunun mühendislik özelliklerinin değişimi karşılaştırılmıştır. Sonuç olarak olivinin sıcak karışım asfalt betonlarda filler malzeme olarak kullanılabileceği görülmüştür.

19. yy’dan günümüze kadar geçen zaman içerisinde, geniş olanak yelpazesine sahip mimari yapılar, cam duvarların da kullanılmasıyla hafif, şeffaf ve havadar görüntülü yapıların gelişmesine olanak sunmuştur. Cam üzerinde yapılan teknolojik çalışmalar ve bunun sonucundaki olumlu gelişmeler mimarlar için camı daha çekici bir malzeme yapmıştır. Özellikle çelik ve camın mimari yapılarda birleşmesi saydamlık ve hafiflik yolunu açarak bu alanda yeni gelişmeler sağlamıştır. Görünen o ki camın gelişmeye açık bir malzeme olduğu gün geçtikçe daha çok kabul edilmekte ve cam mimari artık strüktürel olarak da yer almaktadır. Bir zamanlar bir ütopyadan ibaret olan cam mimarisi günümüzde artık bir gerçek haline gelmiştir. Bu anlamda bu çalışma içerisinde 9 adet mimari yapı ele alınmış ve yapısal olarak incelenerek cam binalara örnek olarak sunulmuştur.

This study systematically investigates the combined effects of three different glass fiber lengths (3, 6, and 12 mm) and three different fiber ratios (1%, 2%, and 3%) on the physical, mechanical, and microstructural properties of cement mortars. Glass fibers are known to enhance mortar performance, yet the simultaneous influence of fiber length and proportion on fresh, hardened, durability, and microstructural characteristics has not been comprehensively addressed in a single experimental framework. The parameters investigated include flow diameter, dry unit weight, water absorption, flexural and compressive strength (at 7 and 28 days), ultrasonic pulse velocity, water sorptivity, as well as SEM/EDS and XRD analyses. Results demonstrated that increasing fiber length and content decreased flow diameter and increased porosity within the mortar compositions. At a 3% fiber inclusion, dry unit weight values decreased, with the lowest value (below 2100 kg/m³) observed for the 12 mm-3% mixture. Flexural strength results highlighted the critical role of the curing process on fiber-matrix interface development. At 7 days, only 1% fiber content improved flexural strength, while higher contents reduced it. At 28 days, however, increasing fiber content generally enhanced flexural strength, particularly for 6 mm fibers, albeit at the expense of compressive strength. The capillarity test revealed that the optimal fiber proportion was 1%, with mixtures achieving compressive strengths exceeding 50 MPa and capillarity coefficients below 0.10 mm/min^0.5, while higher fiber contents led to elevated capillarity coefficients. The study concluded that, under the specific conditions tested, the most suitable fiber length is 6 mm, with a recommended fiber content of 1–2%. The 6 mm-1% combination delivered the best overall performance, achieving 60.18 MPa compressive strength, a capillarity coefficient below 0.10 mm/min^0.5, and enhanced flexural strength. While increasing fiber content improved flexural strength, it reduced compressive strength and increased the capillarity coefficient. These findings underscore the importance of using appropriate fiber proportions to optimize mortar performance and provide practical guidance for designing fiber-reinforced mortars in structural and construction applications.

Dekorasyon ürünlerinden biri olan seramik aydınlatma ürünleri, evler, oteller ve ayrıca restoranlar için oldukça uygundur. Farklı teknikler ve süslemelerle uygun bir dekorasyon elde etmek, seramik aydınlatma ürünlerinin tasarım ve üretim süreci için temel amaçtır. Tasarım dergilerinde, tasarım içerikli internet sitelerinde endüstriyel ürünler sınıfında yer alan seramik aydınlatma elemanlarına (aksesuarlarına) rastlamak mümkündür. Çalışmanın tasarım sürecinde, doğadaki çeşitlilikten faydalanıp canlılardan, denizden, ağaçtan, denize hayat katan dalgalardan esinlenilmiştir.Bu çalışmada, seramik aydınlatma elemanlarının tasarım önerisine yönelik araştırmalarının yapılması, tasarım önerisinin geliştirilerek akademik ölçekli olarak yazılı kaynak haline getirilmesi amaçlanmıştır.