Magnesium phosphate cement (MPC), a new type of inorganic cementitious material, is favored in engineering and construction because of its fast setting speed and high bonding strength, but is limited in practical application due to its high production cost and excessive release of hydration heat. Relevant research has investigated the application of discarded oyster shell powder (OSP) replacing cement mortar and has reported certain improvements to its performance. Consequently, focusing on discovering more effects of OSP on MPC performance, this study, by using a typical three-point bending test, used 45 cuboid specimens to investigate the influences of OSP mass content on flexural properties of MPC at different curing times. Results illustrated that MPC flexural strength was first increased and then decreased, and 3% is the critical value for OSP mass content. Similarly, the stiffness of all specimens presented a tendency to increase first and then decrease, with a maximum value of 36.18 kN/mm appearing at 3%, i.e., the critical OSP mass content. Finally, scanning electron microscope (SEM) and X-ray diffraction (XRD) were employed to analyze the microstructure and composition of specimens, confirming that the specimens generated not only the hydration product potassium phosphate magnesium (MgKPO₄·6H₂O, MKP), but also another new reactant (CaHPO₄·2H₂O).

The incorporation of coconut fiber (CF) into magnesium phosphate cement (MPC) can effectively improve upon its high brittleness and ease of cracking. In practical engineering, coconut fiber-reinforced magnesium phosphate cement (CF-MPC) will likely work in cold environments. Therefore, it is essential to understand the effects of various types of low-temperature curing on CF-MPC performances, but there are very few studies in this area. In this study, the static compression and three-point bending test were utilized to examine the compressive and flexural characteristics of CF-MPC with various CF contents and different negative curing temperatures. Scanning electron microscopy (SEM) and X-ray diffraction (XRD) were conducted to observe the impact of low-temperature maintenance on the structure and hydration reaction of the specimens. The results indicate that CF-MPC curing at low temperatures was more prone to cracks during compression and bending, while the appropriate amount of CF could enhance its plastic deformation capability. The CF-MPC’s compressive and flexural strength declined as the curing temperature dropped. Moreover, with the rise in CF content, the samples’ compressive strength also tended to fall, and there was a critical point for the change in flexural strength. In addition, MPC’s primary hydration product (MgKPO₄·6H₂O) decreased with a drop in curing temperature, and more holes and fractures appeared in CF-MPC.