In this work the phenomena involved with the microwave devulcanization of ground tyre rubber (GTR) were investigated. During studies three types of GTR characterized by different content of organic compounds (elastomers, plasticizers, etc..), carbon black and ash have been analyzed. The chemical structure of GTR before and after microwave devulcanization process was studied by Fourier transform infrared spectroscopy (FTIR) and thermogravimetric analysis (TGA). Furthermore, efficiency of microwave devulcanization conducted at different time was evaluated based on the crosslinking density and sol content values. FTIR spectroscopy results shown that devulcanization of GTR causes a decrease in carbon black with generation of CO2 due to its thermo oxidation, a decrease in structural groups of elastomeric components (mainly methylene and methine) and a breaking of C-S groups and S-S bridges. The presented results indicate the strong correlation between content of SiO2 in GTR and its degree of devulcanization. It was observed that GTR with a high content of SiO2 are easier devulcanized than samples with low content of SiO2, which suggest the presence of silica fillers improve microwave devulcanization efficiencyPostprint (author's final draft

Ground tire rubber from car and truck was modified using microwave irradiation at variable time. The irradiated ground tire rubber was used as filler in composites based on natural rubber. The composites, with high content of ground tire rubber, were prepared using an internal batch mixer and subsequently cross-linked at 160℃. The influence of the ground tire rubber source (car/truck) and irradiation time on structure, physico-mechanical behaviour, thermal properties and morphology of natural rubber/ground tire rubber composites was studied. The interfacial interactions between ground tire rubber and natural rubber as function of ground tire rubber source and irradiation time were evaluated by Fourier transform infrared spectroscopy, thermogravimetric analysis, tensile tests, swelling measurements and scanning electron microscopy. The results showed that irradiation of ground tire rubber slightly enhanced tensile properties and cross-link density of natural rubber/ground tire rubber composites. This effect was more evident in the case of ground tire rubber_truck because of its higher content of natural rubber and was reflected in changes in the interfacial adhesion, which were confirmed by the results of Fourier transform infrared spectroscopy, thermogravimetric analysis and scanning electron microscopy analysis.