The purpose of the present study was to assess the proper time to perform a restoration (immediately or delayed) after placement of two calcium silicate-based cements (CSCs) and to test the performance of two different restorative protocols regarding shear bond strength (SBS). Seventy-five acrylic blocks were randomly divided into five groups (n = 15). Specimens were filled with either ProRoot MTA (Dentsply Tulsa Dental) or Biodentine (Septodont). The restoration was performed at an immediate (12 min) or delayed (seven days) timeframe, using a resin-based flowable composite (SDR) (bonded to the CSC using a universal bonding system) or glass ionomer cement (GIC) as restorative materials. SBS was measured using a universal testing machine. Fractured surfaces were evaluated, and the pattern was registered. Statistical analysis was performed using the Dunn–Sidak post hoc test (P < 0.05). Biodentine/immediate SDR showed the highest mean SBS value (4.44 MPa), with statistically significant differences when compared to mineral trioxide aggregate (MTA)/GIC (1.14 MPa) and MTA/immediate SDR (1.33 MPa). MTA/GIC and MTA/immediate SDR did not present significant differences regarding SBS. No statistical differences were verified concerning mean SBS between both CSCs within the 7 day groups. MTA/delayed SDR (3.86 MPa) presented statistical differences compared to MTA/immediate SDR, whereas no differences were observed regarding Biodentine performance (Biodentine/immediate SDR and Biodentine/delayed SDR (3.09 MPa)). Bonding procedures directly on top of MTA might be preferably performed at a delayed timeframe, whereas Biodentine might allow for immediate restoration.

The aim of the present ex vivo study was to assess and compare coronal discoloration induced by four endodontic biomaterials used in regenerative endodontic procedures (REPs). Root resection was executed horizontally, 2 mm apical to the cementoenamel junction, in all fifty-four teeth. After accessing the pulp chamber, specimens were randomly divided in groups and filled with either saline solution or blood, followed by calcium silicate-based cements (CSCs) placement: ProRoot mineral trioxide aggregate (MTA) (Dentsply Sirona), Biodentine (Septodont), TotalFill BC (FKG), or pulp capping material (PCM) (Coltène). Color change (ΔE) was assessed using the L* a* b* system at five different timepoints (before and immediately after biomaterial application, 72 h, 7 days, and 6 months). The significance level for statistical analysis was set at p < 0.05. There are statistically significant differences regarding ΔE over time (p < 0.001). Statistical differences are found considering material (p < 0.001), treatment (p = 0.007), or both (p = 0.002). If solely the material or treatment is considered, regardless of time, statistically significant differences are detected (p < 0.001). After a six-month period of evaluation, blood exposure might be a critical factor in biomaterials’ color variation. Biodentine presents the lowest discoloration potential, followed by TotalFill and PCM, albeit without statistically significant differences. MTA exhibited the greatest color variation. The selection of biomaterial should consider the material’s discoloration potential.

Objective: To evaluate the effect of rubber dam isolation on shear bond strength of two different adhesive systems to enamel.Materials and Methods: The mesial, distal, lingual, and vestibular enamel surfaces of thirty human third molars were prepared (total n = 120). A custom splint was made to fit a volunteer's maxilla, holding the specimens in place in the oral cavity. Four composite resin cylinders were bonded to each tooth with one of two bonding agents (OptiBond FL and Prime&Bond active) with or without rubber dam isolation. Shear bond strength was tested in a universal testing machine and failure modes were assessed. Significance level for statistical analyses was set at 5%.Results: All pairwise comparisons revealed statistical differences (p < 0.05). The highest mean shear bond strength values were obtained in rubber dam experimental groups, regardless of the adhesive system. Group OptiBond FL with rubber dam presented the highest mean bond strength values. Fracture modes for specimens bonded without rubber dam isolation were adhesive and cohesive within enamel, while rubber dam experimental groups revealed only cohesive fractures.Conclusions: Absolute isolation with rubber dam increases bond strength to enamel, independent of the adhesive system. The three‐step total‐etch system OptiBond FL provided significantly higher bond strength values than Prime&Bond active under both experimental conditions.Clinical Significance: Rubber dam isolation has a significant effect on bond strengths to enamel, independent of the adhesive system. Its application is, therefore, advised whenever adhesive procedures are performed. A filled three‐step etch‐and‐rinse adhesive performed superiorly, with or without rubber dam isolation, when bonding to enamel compared to an isopropanol‐based universal adhesive.

(1) Background: access cavity preparation is the first stage of non-surgical endodontic treatment. The inaccuracy of this step may lead to numerous intraoperative complications, which impair the root canal treatment’s prognosis and therefore the tooth’s survival. Guided endodontics, meaning computer-aided static (SN) and dynamic navigation (DN) techniques, has recently emerged as a new approach for root canal location in complex cases. This review aims to compare SN and DN guided endodontics’ techniques in non-surgical endodontic treatment. (2) Methods: an electronic search was performed on PubMed, Scopus, and Cochrane Library databases until October 2021. Studies were restricted by language (English, Spanish and Portuguese) and year of publication (from 2011 to 2021). (3) Results: a total of 449, 168 and 32 articles were identified in PubMed, Scopus, and Cochrane Library databases, respectively, after the initial search. Of the 649 articles, 134 duplicates were discarded. In this case, 67 articles were selected after title and abstract screening, of which 60 were assessed for eligibility through full-text analysis, with one article being excluded. Four cross-references were added. Thus, 63 studies were included. (4) Conclusions: guided endodontics procedures present minimally invasive and accurate techniques which allow for highly predictable root canal location, greater tooth structure preservation and lower risk of iatrogenic damage, mainly when performed by less experienced operators. Both SN and DN approaches exhibit different advantages and disadvantages that make them useful in distinct clinical scenarios.

Collagenated porcine-derived bone graft materials exhibit osteoconductive properties and the development of different formulations intends to enhance bone regeneration. This study aims to evaluate bone healing in a rabbit cancellous bone defect in response to grafting with different physicochemical forms of heterologous porcine bone. Twenty-six adult male New Zealand White rabbits received two critical size femoral bone defects per animal (n = 52), each randomly assigned to one of the five tested materials (Apatos, Gen-Os, mp3, Putty, and Gel 40). Animals were sacrificed at 15- and 30-days post-surgery. Qualitative and quantitative (new bone, particle and connective tissue percentages) histological analyses were performed. Histomorphometry showed statistically significant differences in all evaluated parameters between mp3 and both Putty and Gel 40 groups, regardless of the timepoint (p < 0.05). Moreover, statistical differences were observed between Apatos and both Putty (p = 0.014) and Gel 40 (p = 0.007) groups, at 30 days, in regard to particle percentage. Within each group, regarding new bone formation, mp3 showed significant differences (p = 0.028) between 15 (40.93 ± 3.49%) and 30 (52.49 ± 11.04%) days. Additionally, intragroup analysis concerning the percentage of particles revealed a significant reduction in particle occupied area from 15 to 30 days in mp3 and Gen-Os groups (p = 0.009). All mp3, Gen-Os and Apatos exhibited promising results in terms of new bone formation, thus presenting suitable alternatives to be used in bone regeneration.