Incorporation of mesopores and active sites into metal-organic framework (MOF) materials to uncover new efficient catalysts is a highly desirable but challenging task. We report the first example of a mesoporous MOF obtained by templated electrosynthesis using an ionic liquid as both electrolyte and template. The mesoporous Cu(II)-MOF MFM-100 has been synthesised in 100 seconds at room temperature, and this material incorporates crystal defects with uncoupled Cu(II) centres as evidenced by confocal fluorescence microscopy and electron paramagnetic resonance spectroscopy. MFM-100 prepared in this way shows exceptional catalytic activity for the aerobic oxidation of alcohols to produce aldehydes in near quantitative yield and selectivity under mild conditions, as well as having excellent stability and reusability over repeated cycles. The catalyst-substrate binding interactions have been probed by inelastic neutron scattering. This study offers a simple strategy to create mesopores and active sites simultaneously via electrochemical formation of crystal defects to promote efficient catalysis using MOFs.

The demand for xylenes is projected to increase over the coming decades. The separation of xylene isomers, particularly p- and m-xylenes, is vital for the production of numerous polymers and materials. However, current state-of-the-art separation is based upon fractional crystallisation at 220 K which is highly energy intensive. Here, we report the discrimination of xylene isomers via refinement of the pore size in a series of porous metal–organic frameworks, MFM-300, at sub-angstrom precision leading to the optimal kinetic separation of all three xylene isomers at room temperature. The exceptional performance of MFM-300 for xylene separation is confirmed by dynamic ternary breakthrough experiments. In-depth structural and vibrational investigations using synchrotron X-ray diffraction and terahertz spectroscopy define the underlying host–guest interactions that give rise to the observed selectivity (p-xylene < o-xylene < m-xylene) and separation factors of 4.6–18 for p- and m-xylenes.

FTIR absorption micro-spectroscopy is a widely used, powerful technique for analysing biological materials. In principle it is a straightforward linear absorption spectroscopy, but it can be affected by artefacts that complicate the interpretation of the data. In this article, artefacts produced by the electric-field standing-wave (EFSW) in micro-reflection-absorption (transflection) spectroscopy are investigated. An EFSW is present at reflective metallic surfaces due to the interference of incident and reflected light. The period of this standing wave is dependent on the wavelength of the radiation and can produce non-linear changes in absorbance with increasing sample thickness (non-Beer–Lambert like behaviour). A protein micro-structure was produced as a simple experimental model for a biological cell and used to evaluate the differences between FTIR spectra collected in transmission and transflection. By varying the thickness of the protein samples, the relationship between the absorbance and sample thickness in transflection was determined, and shown to be consistent with optical interference due to the EFSW coupled with internal reflection from the sample top surface. FTIR spectral image data from MCF 7 breast adenocarcinoma cells was then analysed to determine the severity of the EFSW artefact in data from a real sample. The results from these measurements confirmed that the EFSW artefact has a profound effect on transflection spectra, and in this case the main spectral variations were related to the sample thickness rather than any biochemical differences.

Capture of trace benzene is an important and challenging task. Metal–organic framework materials are promising sorbents for a variety of gases, but their limited capacity towards benzene at low concentration remains unresolved. Here we report the adsorption of trace benzene by decorating a structural defect in MIL-125-defect with single-atom metal centres to afford MIL-125-X (X = Mn, Fe, Co, Ni, Cu, Zn; MIL-125, Ti₈O₈(OH)₄(BDC)₆ where H₂BDC is 1,4-benzenedicarboxylic acid). At 298 K, MIL-125-Zn exhibits a benzene uptake of 7.63 mmol g⁻¹ at 1.2 mbar and 5.33 mmol g⁻¹ at 0.12 mbar, and breakthrough experiments confirm the removal of trace benzene (from 5 to <0.5 ppm) from air (up to 111,000 min g⁻¹ of metal–organic framework), even after exposure to moisture. The binding of benzene to the defect and open Zn(II) sites at low pressure has been visualized by diffraction, scattering and spectroscopy. This work highlights the importance of fine-tuning pore chemistry for designing adsorbents for the removal of air pollutants.