Green synthesis of gold nanoparticles (GNPs) with plant extracts has gained considerable interest in the field of biomedicine. Recently, the bioreduction nature of herbal extracts has helped to synthesize spherical GNPs of different potential from gold salt. In this study, a fast ecofriendly method was adopted for the synthesis of GNPs using fresh peel (aqueous) extracts of Benincasa hispida, which acted as reducing and stabilizing agents. The biosynthesized GNPs were characterized by UV–VIS and Fourier transform infrared spectroscopy, transmission electron microscopy (TEM), and dynamic light scattering. In addition, the in vitro antibacterial and anticancer activities of synthesized GNPs were investigated. The formation of gold nanoparticles was confirmed by the existence of a sharp absorption peak at 520 nm, corresponding to the surface plasmon resonance (SPR) band of the GNPs. TEM analysis revealed that the prepared GNPs were spherical in shape and had an average particle size of 22.18 ± 2 nm. Most importantly, the synthesized GNPs exhibited considerable antibacterial activity against different Gram-positive and Gram-negative bacteria. Furthermore, the biosynthesized GNPs exerted remarkable in vitro cytotoxicity against human cervical cancer cell line, while sparing normal human primary osteoblast cells. Such cytotoxic effect was attributed to the increased production of reactive oxygen species (ROS) that contributed to the damage of HeLa cells. Collectively, peel extracts of B. hispida can be efficiently used for the synthesis of GNPs, which can be adopted as a natural source of antimicrobial and anticancer agent.

Baricitinib is a recently approved anti-rheumatic drug having very poor aqueous solubility and hence its performance suffers from low or inconsistent oral bioavailability. The purpose of the study was to develop and evaluate poly lactic-co-glycolic acid (PLGA) nanoparticles of baricitinib in order to enhance in vitro dissolution and performance. Nano-suspension of baricitinib with or without PLGA, a biodegradable, FDA approved semi-synthetic polymer, was developed by nanoprecipitation method. Research methodology employed a quantitative research utilizing experimental design wherein effect of independent variables such as amount of polymer, drug: polymer ratio, types of solvent, and solvent: anti-solvent ratio were evaluated over the size and size distribution of nanoparticles along with entrapment efficiencies. Among the several organic phases evaluated, acetone was found to be suitable solvent for drug and polymer. The aqueous phase (anti-solvent) was deionized water containing 1% w/v pluronic 127 as the stabilizer of nanoparticle suspension. The optimized nanoparticles had particle size less than 100 nm (91 nm ± 6.23) with a very narrow size distribution (0.169 ± 0.003), high zeta potential (-12.5 mV ± 5.46) and entrapment efficiency (88.0%). The optimized nanoparticles were characterized by scanning electron microscopy, X-ray diffraction, differential scanning calorimetry, infrared spectroscopy and in vitro dissolution studies. In-vitro dissolution study of PLGA nanoparticles exhibited sustained release with approximately 93% release of baricitinib during 24-h period.