The nasal drug delivery route has distinct advantages, such as high bioavailability, a rapid therapeutic effect, non-invasiveness, and ease of administration. This article presents the results of a study of the processes for obtaining chitosan aerogel particles that are promising as nasal or inhalation drug delivery systems. Obtaining chitosan aerogel particles includes the following steps: the preparation of a chitosan solution, gelation, solvent replacement, and supercritical drying. Particles of chitosan gels were obtained by spraying and homogenization. The produced chitosan aerogel particles had specific surface areas of up to 254 m²/g, pore volumes of up to 1.53 cm³/g, and porosities of up to 99%. The aerodynamic diameters of the obtained chitosan aerogel particles were calculated, the values of which ranged from 13 to 59 µm. According to the calculation results, a CS1 sample was used as a matrix for obtaining the pharmaceutical composition “chitosan aerogel—clomipramine”. X-ray diffraction (XRD) analysis of the pharmaceutical composition determined the presence of clomipramine, predominantly in an amorphous form. Analysis of the high-performance liquid chromatography (HPLC) data showed that the mass loading of clomipramine was 35%. Experiments in vivo demonstrated the effectiveness of the pharmaceutical composition “chitosan aerogel—clomipramine” as carrier matrices for the targeted delivery of clomipramine by the “Nose-to-brain” mechanism of nasal administration. The maximum concentration of clomipramine in the frontal cortex and hippocampus was reached 30 min after administration.

The research was oriented towards the preparation of aerogel particles based on egg white and whey protein isolate using various dispersion methods: dripping, spraying, and homogenization. Based on the results of analytical studies, the most appropriate samples were selected to obtain aerogels loaded with the drug. The results of the experimental research were used to study methods for obtaining nasal drug delivery systems based on aerogels. Protein aerogels were obtained by thermal gelation followed by supercritical drying. The obtained particles of protein aerogels have a specific surface area of up to 350 m²/g with a pore volume of up to 2.9 cm³/g, as well as a porosity of up to 95%. The results of experimental studies have shown that changing the dispersion method makes it possible to control the structural characteristics of protein aerogel particles. The results of the studies were applied to obtain innovative nasal drug delivery systems for the treatment of socially significant diseases. Analytical studies were conducted to determine the amount and state of adsorbed drugs in protein aerogel particles, as well as in vivo experiments on the distribution of clomipramine in blood plasma and brain tissue of rats to study the pharmacokinetics and bioavailability of the resulting drug-loaded protein aerogel.

Three-dimensional (3D) printing is a promising technology for solving a wide range of problems: regenerative medicine, tissue engineering, chemistry, etc. One of the potential applications of additive technologies is the production of highly porous structures with complex geometries, while printing is carried out using gel-like materials. However, the implementation of precise gel printing is a difficult task due to the high requirements for “ink”. In this paper, we propose the use of gel-like materials based on sodium alginate as “ink” for the implementation of the developed technology of extrusion-based 3D printing. Rheological studies were carried out for the developed alginate ink compositions. The optimal rheological properties are gel-like materials based on 2 wt% sodium alginate and 0.2 wt% calcium chloride. The 3D-printed structures with complex geometry were successfully dried using supercritical drying. The resulting aerogels have a high specific surface area (from 350 to 422 m²/g) and a high pore volume (from 3 to 3.78 cm³/g).

Natural compounds are becoming increasingly popular in the fields of pharmaceuticals and cosmetics. One such compound is lignin, a plant-derived aromatic polymer that serves as a natural anti-ultraviolet agent. Conventional methods for extracting lignin from plant materials typically involve performing procedures in harsh environments, such as dissolving it in highly alkaline solutions or subjecting it to treatment in acidic conditions. In this study, lignin was extracted from coconut husk under milder conditions, using neutral solvents and ultrasonic treatment, which allowed us to obtain lignin with significantly improved properties. The developed method facilitated the creation of light-colored lignin, which was employed as a natural ingredient in sunblock cream. Furthermore, for the sake of comparison, lignin was extracted under more rigorous conditions using the traditional method. The research findings confirm that the light-colored lignin sample exhibits a higher level of UV absorption. Furthermore, light-colored lignin demonstrates a synergistic effect when combined with commercial moisturizing creams and sunscreens, leading to a significant enhancement in their SPF performance against both UVA and direct sunlight exposure. This study highlights the potential value of incorporating lignin as a valuable natural ingredient in sunblock and cosmetic products.

The manuscript describes methods for producing hybrid silica microparticles and hybrid alginate beads with carbon nanotube (CNT) contents up to 4.5 and 30 wt.%, respectively. Silica hybrid aerogel microparticles with embedded nanotubes were obtained using a two-stage sol–gel method with a gelling process in an oil-emulsion. Alginate hybrid aerogels with embedded nanotubes were obtained using cross-linking reactions. The following methods were used to measure the structural characteristics of obtained materials: nitrogen adsorption porosimetry, scanning electron microscopy (SEM), and others. It is shown that specific surface area and pore volume increase with the increase of CNT content in silica aerogel microparticles. Obtained aerogels were tested as adsorbents for argon–oxygen separation. The alginate hybrid aerogel with 30 wt.% CNT content has the best argon adsorption selectivity.

The presented work is devoted to isocyanate synthesis by the thermal decomposition of carbamates model. The work describes the existing isocyanate-obtaining processes and the main problems in the study of isocyanate synthesis by the thermal decomposition of carbamates, which can be solved using mathematical and computer models. Experiments with carbamates of various structures were carried out. After processing the experimental data, the activation energy and the pre-exponential factor for isocyanate synthesis by the thermal decomposition of carbamates were determined. Then, a mathematical model of the reactor for the thermal decomposition of carbamates using the COMSOL Multiphysics software was developed. For this model, computational experiments under different conditions were carried out. It was shown that the calculation results correspond to the experimental ones, so the suggested model can be used in the design of the equipment for isocyanate synthesis by the thermal decomposition of carbamates.