The aim of this in vitro study was to evaluate the dentinal tubule penetration of two calcium silicate-based sealers used in warm vertical compaction (WVC) obturation technique in comparison with the single cone (SC) technique by confocal laser scanning microscopy (CLSM). The null hypothesis was that both obturation techniques produced similar sealer penetration depths at 1 and 5 mm from the apex. Forty-four mandibular single-rooted premolars were randomly divided into four equally experimental groups (n = 10) and two control groups (n = 2) according to the type of sealer (Bio-C Angelus, Londrína, PR, Brazil or HiFlow Brasseler, Savannah, GA, USA) with either SC or WVC. The sealers were mixed with a fluorescent dye Rhodamine B (0.1%) to enable the assessment under the CLSM. All the specimens were sectioned horizontally at 1 and 5 mm from the apex. The maximum penetration depth was calculated using the ImageJ Software (ImageJ, NIH). Data were analyzed by Mann–Whitney U and Kruskal–Wallis tests (p < 0.05). A significant difference was shown between the four groups at 1 mm (p = 0.0116), whereas similar results were observed at 5 mm (p = 0.20). WVC allowed better diffusion for both sealers at 1 mm (p = 0.01) and 5 mm (p = 0.034). The maximum penetration of the Bio-C and HiFlow sealers was more important at 5 mm with the two obturation techniques. Within the limitations of this study, WVC enhanced the penetration of calcium silicate-based sealers into the dentinal tubules in comparison with the SC technique at both levels.

We assessed the efficiency of two shaping file systems and two passive ultrasonic irrigation (PUI) devices for removing filling material during retreatment. The mesial canals from 44 extracted mandibular molars were prepared and obturated. The teeth were randomly divided into two groups, and then one group was retreated with Reciproc R25 (VDW, Munich, Germany) (n = 44) and the other group was retreated with 2Shape (TS, Micro Mega, Besançon, France) (n = 44). A micro-computed tomography (CT) scan was taken before and after the retreatment to assess the volume of the filling material remnants. The teeth were then randomly divided into four groups to test two different PUI devices: Irrisafe (Satelec Acteon Group, Merignac, France) and Endo Ultra (Vista Dental Products, Racine, WI, USA). The teeth in Group A were retreated with 2Shape to test the Endo Ultra (n = 22) device, the teeth in Group B were retreated with 2Shape in order to test the Irrisafe (n = 22) device, the teeth in Group C were retreated with Reciproc to test the Endo Ultra (n = 22) device, and Group D was retreated with Reciproc to test the Irrisafe (n = 22) device. A third micro-CT scan was taken after the retreatment to test the PUIs. The percentage of Gutta-Percha (GP) and sealer removed was 94.75% for TS2 (p < 0.001) and 89.3% for R25 (p < 0.001). The PUI significantly enhanced the removal of the filling material by 0.76% for Group A (p < 0.001), 1.47% for Group B (p < 0.001), 2.61% for Group C (p < 0.001), and by 1.66% for Group D (p < 0.001). 2Shape was more effective at removing the GP and sealer during retreatment (p = 0.018). The supplementary approach with PUI significantly improved filling material removal, with no statistical difference between the four groups (p = 0.106).

We compared the mechanical properties of 2Shape mini TS2 (Micro-Mega, Besançon, France) obtained from 1.0 diameter nickel-titanium (NiTi) wires and 2Shape TS2 from 1.2 diameter nickel-titanium (NiTi) wires differently thermally treated at room and body temperature. We used 120 NiTi TS2 1.0 and TS2 1.2 files made from controlled memory (CM) wire and T-wire (n = 10). Cyclic fatigue resistance was tested by recording the number of cycles to fracture (NCF) at room and body temperatures using a customized testing device. Maximum torque and angle of rotation at failure were recorded, according to ISO 3630-1. Data were analyzed by a two-way ANOVA (p < 0.05). The CM-wire files had significantly higher NCFs at both temperatures, independent of wire dimensions. Testing at body temperature negatively affected cyclic fatigue of all files. The 1.0-mm diameter T-wire instruments showed higher NCF than the 1.2-mm diameter, whereas no significant differences emerged between the two CM wires at either temperature. The maximum torque was not significantly different across files. The TS2 CM-wire files showed significantly higher angular rotation to fracture than T-wire files. The TS2 CM-wire prototypes showed higher cyclic fatigue resistance than T-wire prototypes, regardless of wire size, exhibiting suitable torsional properties. Torsional behavior appears to not be affected by NiTi wire size.

Objectives: The aim of this study was to investigate the root anatomy of the maxillary and mandibular premolars among a sample of the Lebanese population and to explore their incidence by sex and the symmetry between the left and right sides. Materials and Methods: This retrospective analysis of 250 cone-beam computed tomography (CBCT) scans consisted of 960 maxillary and 972 mandibular premolars. Roots, canals, and morphology types were recorded. Vertucci’s classification was used to categorize the canal morphologies. Fisher’s exact and chi-square tests were applied (P≤.05). Results: The majority of maxillary first premolars had two roots (85.3%) with two canals (91.3%). Most of the maxillary second premolars showed one root (79.8%). Two-root canals (53.55%) were more common than one canal (44.2%). The three-root, three-canal morphology was rarely spotted in the maxillary first (0.4%) and second premolars (2.3%). The one-root (99.2%) and one-canal (84.5%) morphologies were most frequently located in the mandibular first and second premolars (100%, 88.6%), and two canals being less common (15.5%, 11.4%) correct same as before. The total prevalence of premolars with a complex root canal morphology was 62.4%, found in types II, III, and V to VIII. Men had significantly more roots and root canals in their maxillary first premolars than women (P≤.05). No significant differences were observed between the contralateral premolars (P>.05). Conclusions: Premolars displayed wide variations in root and root canal morphology and symmetry between the contralateral premolars.