In this research, we successfully fabricate high-hardness and lightweight Al-Ti composites. Al-Ti composites powders with three compositions (Al-20, 50, and 80 vol.% Ti) are mixed using ball milling and subsequently subjected to spark plasma sintering (SPS). The microstructures and phases of the Al-Ti composites are characterized using scanning electron microscopy (SEM), X-ray diffraction (XRD) spectroscopy, and field emission-electron probe microanalysis (FE-EPMA). These tests confirm the presence of several intermetallic compounds (ICs) (Al₃Ti, Al₅Ti₂, Al₁₁Ti₅) in the composites, and we are able to confirm that these ICs are produced by the reaction of Al and Ti during the SPS process. Furthermore, thermogravimetric-differential thermal analysis (TG-DTA) is used to analyze the formation behavior of the ICs. In addition, the mechanical properties of the composites are measured using their Vickers hardness and it is observed that the Al-80 vol.% Ti composite exhibits the highest hardness. Consequently, it is assumed that SPS is suitable for fabricating Al-Ti composites which represent the next-generation materials to be used in various industrial fields as high-hardness and lightweight materials.

In this study, we have attempted to manufacture functionally graded materials (FGMs) using aluminum alloys 3003 and 6063 via a hot extrusion process to realize multifunctionality through achieving high strength and low weight. The FGMs were fabricated using Al3003 powder and Al6063 bulk to improve the interfacial properties. Particle size analysis and X-ray fluorescence of the Al3003 powder were used to analyze the composition of general Al3003; microstructure analysis revealed improved hardness with almost no defects, such as cracks at the interface between the two materials. The experimentally determined tensile strength of the composite was observed to be higher than the theoretical value calculated using the rule of mixtures; the strengthening mechanisms considered for the calculations were grain size reduction and precipitation hardening. In particular, we attempted to predict the strengthening effect resulting from the fine grain size of the powder and grain size reduction due to the extrusion process using the Hall–Petch equation. The Kelly–Tyson equation was also used to calculate the theoretical strength in the presence of the strengthening phases. Based on these results, it was confirmed that FGMs can be successfully produced using the hot extrusion process.