Atomizing discharge ablation milling (ADAM) technology is an efficient discharge machining technology derived from the traditional electrical discharge machining (EDM) method, which can be used to efficiently machine hard-to-machine materials such as nickel-based superalloy. In this present, the performance of machining nickel-based superalloy GH4145 by ADAM and Air near-dry EDM were compared, and the experimental results showed that the material removal rate (MRR) obtained by ADAM was nearly double that of the latter. A single-factor experiment were conducted to investigate the effect of electrode rotation speed on ADAM’s processing performance. Subsequently, an orthogonal experimental method was used to design the experiment. The signal-to-noise ratio analysis method was used to systematically study the performance characteristics of ADAM, including the influence of atomization amount, oxygen pressure, discharge current, duty ratio on MRR and tool electrode relative wear rate (TWR). The results showed that discharge current was the most influential processing parameter on MRR and TWR. Finally, the optimal combination of processing process parameters that met the requirements of various processing effect evaluation indicators were obtained and the correctness of the single objective optimization results was verified through experiments.

To meet the demands for lightweight design and high-conductivity connections in new energy vehicles, the high-quality joining of dissimilar Al/Cu metals has emerged as a critical research focus. In this study, laser welding was performed on 2 mm-thick 1060 pure aluminum and T2 copper plates. The effects of laser power (3.6–4.0 kW) and welding speed (0.9–1.5 m/min) on the interfacial microstructural evolution and mechanical properties of the lap joints were systematically investigated. The results demonstrate that the macroscopic morphology of the weld is primarily governed by heat input: excessive laser power induces transverse cracking, whereas an overly low welding speed promotes porosity. Microstructural analysis revealed that intermetallic compounds (IMCs), such as Al₂Cu, AlCu, and Al₄Cu₉, predominantly form at the interface, with their morphology and distribution varying significantly depending on the heat input. Under the optimized parameters of a 3.8 kW laser power and a 1.2 m/min welding speed, sufficient mixing of the molten Al and Cu was achieved. This promoted the formation of fine, dispersed IMCs accompanied by a continuous Al–Cu eutectic layer at the interface, yielding a maximum tensile-shear load of 1561 N. This research elucidates the intrinsic relationship between heat input and the microstructure–property correlation of Al/Cu laser-welded joints, identifying a viable process window for 2 mm-thick sheets and providing theoretical and practical guidance for joining dissimilar medium-thickness metal plates.